Corrosion Behavior of Structural Ceramics in Supercritical Water
スポンサーリンク
概要
- 論文の詳細を見る
The corrosion behavior of Si3N4 SiC, mullite, alumina and sapphire was investigated in supercritical water at 450°C and 45MPa for 2 to 50h. Corrosion resistance for the ceramics was as follows in the order; Si3N4<SiC<mullite<alumina<sapphire. Pitting corrosion with formation of amorphous layer and intergranular corrosion due to dissolution of additives were observed in PLS-Si3N4 and PLS-SiC, respectively. The corrosion behavior of mullite was characterized by dissolution of SiO2 and formation of boehmite residue layer. High purity alumina ceramics showed the highest corrosion resistance in the ceramics. Intergranular corrosion proceeded in the alumina ceramics and its corrosion rate was strongly dependent on the impurity content.
- 社団法人 腐食防食協会の論文
社団法人 腐食防食協会 | 論文
- Resistance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Renietance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Resistance of Monel Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Symposium on Control of Internal Corrosion of Tankers
- タイトル無し