Effect of Heat Treatment on Intergranular Corrosion for the Weldment of Co Based Alloy

概要

論文の詳細を見る
The influence of heat treatment conditions on intergranular corrosion (IGC) was investigated for the weldments of the Co-based alloy, Stellite by gas welding. The Stellite has IGC susceptibility when it is heated at temperatures ranging from 693 to 973K after welding. It is clarified that this IGC susceptibility of weldments which are subjected to post-weld heat treatment is due to the formation of the grainboundary Cr depletion zone which resulted from precipitation of the M7C3 type Cr carbides. It is also clarified that the grainboundary precipitation of the secondary complex M23C6 carbides consisting of W-Co-Cr-C which are induced by heating above around 1000K suppresses the IGC in Stellite equivalent to production because of mitigation of Cr-depleted zones formation.