The Critical Depth for Pits on Carbon Steel in the Concentrated Aqueous Solution of Lithium Bromide Containing Nitrate at Elevated Temperatures
スポンサーリンク
概要
- 論文の詳細を見る
Pitting corrosion behaviors for carbon steels in an aqueous solution of 60%LiBr+0.2% LiOH+0.2%LiNO3 at 150°C were investigated. Similar to the carbon steel in an aqueous solution of 60%LiBr+0.2% LiOH+0.2%Li2CrO4 which was described in the previous paper, the possibility for the initiation of a growing macro-pit was detected by applying the critical depth concept. The pitting potential, Vc, pit the film breakdown potential, Ez, and the pit repassivation potential, ER, pit were measured to be -480, -490 and-540mV, respectively. And the critical depth, r*, was determined to be 10μm. When a carbon steel was merely immersed in the solution, it reached the steady state in a few hours; micro-pits which were shallower than r* generated intermittently and the initiation of growing macro-pits was inhibited. However, when the carbon steel which was held at-800mV for longer than 10h in the solution prior to the open-circuit immersion as a pretreatment, pits that grew beyond r* during the initial period of the immersion were found to continue growing with a rate of 7mm/y. The pretreatment strengthened the resistance to film breakdown and activated the cathodic reaction on the steel surface. These effects of the pretreatment were found to be more significant for steels in the LiNO3 added solution than those in the Li2CrO4 added solution.
- 社団法人 腐食防食協会の論文
社団法人 腐食防食協会 | 論文
- Resistance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Renietance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Resistance of Monel Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Symposium on Control of Internal Corrosion of Tankers
- タイトル無し