Corrosion Properties of Cu-P Bearing Low Alloy Steels Exposed to the Saline Environments with the Cyclic Variation between Wet and Dry
スポンサーリンク
概要
- 論文の詳細を見る
Paid particular attention to the characteristics of rust layers, this study was conducted to research the corrosion behavior of low-alloy steel containing small amounts of Cu and P in the saline environment which composes cyclic variation between wet and dry periods. Corrosion resistance of the low-alloy steel depends on the relative humidity of atmosphere in dry periods. According to the results of the X-ray diffraction analysis of rust layers and polarization measurements, cathodic reaction of the low-alloy steel exposed to this environment is reduction of β and γ FeOOH to Fe3O4. EPMA analysis of rust layers indicates that localized corrosion of low-alloy steel proceeds in chloride nest to which chloride ions are concentrated. The tight rust layer containing Cu acts as effective barrier to the permeation of chloride ions.
- 社団法人 腐食防食協会の論文
社団法人 腐食防食協会 | 論文
- Resistance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Renietance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Resistance of Monel Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Symposium on Control of Internal Corrosion of Tankers
- タイトル無し