Effect of Phenol Resin Addition on Corrosion Resistance of Aluminum Sheet Coated with Epoxy Resin Using Electrodeposition Process
スポンサーリンク
概要
- 論文の詳細を見る
Effect of phenol resin addition on corrosion resistance of aluminum sheet coated with epoxy resin using electrodeposition process has been investigated. Corrosion test results revealed that the weight loss of the aluminum sheet in 1wt% NaCl solution (311K, pH3.0) decreased with an increase of phenol resin addition to epoxy resin. It was found that glass transition temperature (Tg) and effective network density (ν) of the electrodeposition film were independent of phenol resin addition, but that water absorption and water permeability decreased with an increase of phenol resin addition. Water permeability was correlated well with the corrosion resistance. Corrosion behavior of epoxy resin coated aluminum is discussed in terms of physical properties of electrodeposition film against water in the coating film.
- 社団法人 腐食防食協会の論文
社団法人 腐食防食協会 | 論文
- Resistance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Renietance of Monel, Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Resistance of Monel Nickel and High-Nickel Alloys to Corrosion by Sulfuric Acid
- Symposium on Control of Internal Corrosion of Tankers
- タイトル無し