The Activation Effects of Ca (OH) <SUB>2</SUB> on the Hydration of Glassy Gehlenite
スポンサーリンク
概要
- 論文の詳細を見る
Glass with the gehlenite composition (glassy gehlenite for short) is known as a main phase of granulated blastfurnace slag, and also as a noncrystalline part of aluminous cement. The activation effects, of Ca (OH) <SUB>2</SUB> on the hydration of synthesized glassy gehlenite was investigated and compared with NaOH..A mixture of CaCO<SUB>3</SUB>, Al<SUB>2</SUB>O<SUB>3</SUB> and SiO<SUB>2</SUB> in the mole ratio of C<SUB>2</SUB>AS was melted in a radio-frequency electric furnace at 1700°C, and then quenched into water immediately. The hydration of glassy gehlenite was initiated by an activating agent such as NaOH or Ca (OH) <SUB>2</SUB>. The concentration of various ions in the solution was measured as a function of time by using ICP, and ion chromatography. When glassy gehlenite was dispersed into suspension of Ca (OH) <SUB>2</SUB>, the remarkable elution stage of Al (OH) <SUB>4</SUB><SUP>-</SUP> was observed in the hydration process, subsequently, C<SUB>2</SUB>ASH<SUB>8</SUB> and C-S-H (I) were formed.<BR>The binding energy of each atoms on the particle surface of unhydrated glass was obtained by ESCA. Hence, half width of spectrum of Si 2p orbital differed crystal and glassy gehlenite. It was recognized that the hydration of glassy gehlenite were depended by structure of particle surface.
- 無機マテリアル学会の論文
無機マテリアル学会 | 論文
- 建築の凹凸仕上げ模様の計測方法
- 半水セッコウの凝結時間および硬化体の強さに及ぼす二水セッコウ添加の影響
- セッコウ硬化体の強さに及ぼす半水セッコウスラリーへの超音波照射の影響
- アルミニウム置換型トバモライトの層間を利用した赤色発光する蛍光体の合成と蛍光特性
- 超音波照射を用いて合成した炭酸カルシウムの特徴