The Influence of Additives on the Expansive Stress of Quick Lime
スポンサーリンク
概要
- 論文の詳細を見る
In previous report, authors mentioned that blown out shot occured using only quick lime, and approximately 100kg f/cm<SUP>2</SUP> of expansive stress was obtained when adding retarding agent to hard burned quick lime. <BR>In this report, the influence of additives such as cement minerals and super plasticizer on the expansive stress of quick lime was examined. The results are as follows. <BR>1) When adding anhydrite to quick lime, the hydration is slightly delayed and 100kg f/cm<SUP>2</SUP> of expansive stress is obtained.<BR>2) When adding calcium aluminate to quick lime, the hydration is not delayed at all and it is impossible to charge it into the pipe.<BR>3) Alite possesses large delaying effect on CaO hydration among additives, and expansive stress of quick lime added it reaches 160kg f/cm<SUP>2</SUP>. The reason of this is assumed that the expansion of CaO works effectively on side wall as expansive stress because of self-hardening property of alite.<BR>4) When adding super plasticizer to CaO-Alite, expansive stress increases enormously to more than 300kg f/cm<SUP>2</SUP>.
- 無機マテリアル学会の論文
無機マテリアル学会 | 論文
- 建築の凹凸仕上げ模様の計測方法
- 半水セッコウの凝結時間および硬化体の強さに及ぼす二水セッコウ添加の影響
- セッコウ硬化体の強さに及ぼす半水セッコウスラリーへの超音波照射の影響
- アルミニウム置換型トバモライトの層間を利用した赤色発光する蛍光体の合成と蛍光特性
- 超音波照射を用いて合成した炭酸カルシウムの特徴