The corrosion behaviour of silver brazed SUS 304 stainless steel has been studied in 0.4M NaCl solutions with additions of CuCl<SUB>2</SUB>⋅2H<SUB>2</SUB>O up to 0.05M. Effects of filler alloy composition and copper in solutions on the corrosion behaviour were discussed. Simultaneous corrosion of filler alloy and stainless steel at brazed interface took place. To evaluate each corrosion rate, a new specimen shape, filler alloy was flown along the stainless steel groove with the radius of 2.5 mm, was used. Major elements of filler alloys and stainless steel except silver were dissolved into the solution. The corrosion of filler alloy was the preferencial dissolution of α-Cu (mainly Cu-Zn) phase. Filler alloys containing cadmium and indium had lesser corrosion resistance than Ag-Cu-Zn ternary alloys and exhibited rapid interfacial corrosion.<BR>Corrosion rates of filler alloys and interface were found to depend greatly on the copper content in chloride solution. Copper increased the corrosion rate mainly by the enhancement of cathodic reaction. Over the range of this study, BAg-4 filler alloy was suitable for the corrosion resistant SUS 304 braze joint.
- 一般社団法人 溶接学会の論文
一般社団法人 溶接学会 | 論文
- Special issue. New frontiers of welding technology. Design of super sky scyaper and its conection and welding.
- The Microstructure of Iron Base Binary Weld Metals (Report 2):Effect of ferrite formers
- The Microstructure of Iron Base Binary Weld Metals (Report 1):Effect of austenite forming type alloying elements
- The Behavior of Hydrogen in Arc Welding (Report 4):Hydrogen dissolution into submerged arc weld metal
- A Study on Submerged Arc Welding of HT-80 Steel (Report 1):Cracking and Hydrogen in submerged arc weld metal