Brittle Fracture Initiation Characteristics of Weld Joints for 80 kg/mm<SUB>2</SUB> High Strength Thick Plate Steel (Report 3):Effects of Residual Stress and Repair Welding on Brittle Fracture Initiation from Surface Notch in Fusion Line of Welded Joints
スポンサーリンク
概要
- 論文の詳細を見る
Effects of residual stress and repair welding on the brittle fracture initiation in weld fusion line of the manual arc welded joints for 80kg/mm<SUP>2</SUP> high strength steel were investigated using the wide plate tension test specimen with an angular distortion and a surface notch. And the results were analyzed by application of the fracture mechanics. The main results are summarized as follow:<BR>(1) The maximum residual stress of T-shaped welded joints is about 50kg/mm<SUP>2</SUP> in the direction of weld line. That of repair weld zone is about 35kg/mm<SUP>2</SUP> in the direction of right angle with weld line and is about 50kg/mm<SUP>2</SUP> in the direction of weld line.<BR>(2) The brittle fracture strength of the T-shaped welded wide plate specimen with a surface notch, is lower than that of the transversely welded W(1) specimen. The test results with the specimen in which residual stress is superimposed can be adjusted quantitatively by taking stress intensity factor K<SUB>R</SUB> of Eq. (4) into consideration. The fracture toughness obtained by the above procedure agrees with that of a transversely welded W(1) specimen without residual stress.<BR>(3) The fracture toughness of the repair welded wide plate specimen almost equals to the minimum values of stress relieved welded joints when the notch tip is heated to the temperature range, 300-550°C, in repair welding. Therefore, the fracture stress of the repair welded joints is extremely lowered if defects remain in the fusion line. But it is as high as the fracture stress of the transversely welded W(1) joints as welded, when the maximum temperature of notch tip is below 250°C in repair welding.<BR>(4) It is important that the maximum heat temperature of fusion line is below 250°C in repair welding. Removal ofhydrogen by heating is effective, but its temperature should be below 250°C.<BR>(5) We calculated relation between fracture stress and crack length of T-shaped welded joint and repair weld zone for welded structure.
- 一般社団法人 溶接学会の論文
一般社団法人 溶接学会 | 論文
- Special issue. New frontiers of welding technology. Design of super sky scyaper and its conection and welding.
- The Microstructure of Iron Base Binary Weld Metals (Report 2):Effect of ferrite formers
- The Microstructure of Iron Base Binary Weld Metals (Report 1):Effect of austenite forming type alloying elements
- The Behavior of Hydrogen in Arc Welding (Report 4):Hydrogen dissolution into submerged arc weld metal
- A Study on Submerged Arc Welding of HT-80 Steel (Report 1):Cracking and Hydrogen in submerged arc weld metal