Study on Weld Bond of Dissimilar Welded Joint of α-and γ-Steels (1st Report):On decreasing of weld bond ductilities
スポンサーリンク
概要
- 論文の詳細を見る
In the welding of dissimilar metals such as α-steels (carbon steel, Cr-Mo steel, low alloying steel, etc.) to γ-steels and alloys (austenite stainless steel, Ni alloys, etc.), martensite-like structure at weld bound and macroscopic segregation in weld metal are observed by unsuitable welding procedures and its conditions, and these structures result in lower ductilities of the welds and lead to weld crackings.<BR>Taking notice of such metallurgical phenomena at weld bound and in weld metal, the authors investigated on the substance of martensite-like structure and the effects of chemical compositions of the electrodes and welding conditions on the formation of this structure. Some metallurgical considerations on the macroscopic segregation in weld metal were also discussed.<BR>The formation of martensite-like structure at weld bond in the welding of above dissimilar metals was reduced and the ductility of the welds was improved with increasing Ni content in the electrodes.<BR>Martensite-like structure at weld bond will be formed due to the diffusion of alloying elements such as Ni, Cr, Mo, C, etc. at a stagnation area where flow of the molten metal contacting with the fusion line does not occur. In lower range (less than 35%) of Ni content in weld metal, martensite-like structure at weld bond was formed in large quantity with pre-heating.<BR>Here, the weld bond in the bead-on-plate test specimen of above dissimilar metals, it is not merely as a fusion line, will be defined as a wide semi-melted zone of the base metal that was melted by the molten metal after arc travelling.<BR>Macroscopic segregation in weld metal was greatly observed with increasing welding speed and content of carbide formers as Cr, Mo, V etc. in α-steels, the segregation area was identified as martensite structure partially including carbide.
- 一般社団法人 溶接学会の論文
一般社団法人 溶接学会 | 論文
- Special issue. New frontiers of welding technology. Design of super sky scyaper and its conection and welding.
- The Microstructure of Iron Base Binary Weld Metals (Report 2):Effect of ferrite formers
- The Microstructure of Iron Base Binary Weld Metals (Report 1):Effect of austenite forming type alloying elements
- The Behavior of Hydrogen in Arc Welding (Report 4):Hydrogen dissolution into submerged arc weld metal
- A Study on Submerged Arc Welding of HT-80 Steel (Report 1):Cracking and Hydrogen in submerged arc weld metal