Torsional Delayed Fracture Properties of Induction Heating Quenched and Tempered Spring Steel Wire.
スポンサーリンク
概要
- 論文の詳細を見る
High strength spring steel wire is intensely required for weight saving of coil spring. Induction hardening (quenching & tempering) gives higher strength and stable quality to the spring wire effectively. Generally, higher strength steel becomes more sensitive to hydrogen embrittlement. Relationship between austenite grain size and hydrogen embrittlement is not clear down to date. In this paper, a delayed fracture test under torsional load and a measurement of diffusible hydrogen were carried out using ITW® Induction heating quenched and Tempered Wire with various austenite grain size and various tensile strength. It was revealed that delayed fracture properties were improved by refining of austenite grain size. Improvement was even recognized in super high strength ITW® over 2160N/mm2 grade.
- 日本ばね学会の論文
日本ばね学会 | 論文
- 形状記憶合金への超音波ショットピーニングの影響
- ショットピーニングにより無害化可能な表面欠陥寸法の破壊力学的評価
- ショットピーニング処理後に人工ピットを導入したばね鋼の疲労特性
- ばね鋼の切欠き疲労強度予測
- 鉄粉層内蔵ばね型アクチュエータを用いたリニア平面位置制御機構の開発