Studies on the Flux Action of Soldering (VI):Flux Action of variour Silves Salts and Copper Salts on Ni and Fe Plates
スポンサーリンク
概要
- 論文の詳細を見る
In previous paper, the flux action of various inorganic metal salts (chloride, sulfate and nitrate) for soldering was reported about the relation between the reaction of flux with molten Sn solder and spreadability of Sn solder on Cu plate.<BR>In this report, authors have studied the relation between the reaction of base plate (Ni, Fe) or Sn solder with flux and spreading phenomenon of Sn solder on Fe plate or Ni plate in the case of various silver salts and copper salts as flux.<BR>The results obtained were as follows:<BR>(1) The corrosion rate increases from Ni, to Cu and to Fe.<BR>(2) The effects of corrosion products on spreadability increased from FeCl<SUB>3</SUB>, to FeCl<SUB>2</SUB>, to NiCl<SUB>2</SUB>, and to CuCl<SUB>2</SUB>.<BR>(3) FeSn<SUB>2</SUB> coated on Sn solder obstructs spreading of Sn solder.<BR>(4) FeSn<SUB>2</SUB> produced by the reaction of molten Sn with Fe salt is controlled in proportion to the amount of Ag or Cu in Sn solder.<BR>(5) Spreading of Sn solder on Fe plate is affected by FeSn<SUB>2</SUB> produced at interface of Sn solder and base plate.<BR>(6) When Ni plate is used, Ni dissolves little in Sn solder and spreadability depends on the reactivity of Sn with flux.
- 一般社団法人 溶接学会の論文
一般社団法人 溶接学会 | 論文
- Special issue. New frontiers of welding technology. Design of super sky scyaper and its conection and welding.
- The Microstructure of Iron Base Binary Weld Metals (Report 2):Effect of ferrite formers
- The Microstructure of Iron Base Binary Weld Metals (Report 1):Effect of austenite forming type alloying elements
- The Behavior of Hydrogen in Arc Welding (Report 4):Hydrogen dissolution into submerged arc weld metal
- A Study on Submerged Arc Welding of HT-80 Steel (Report 1):Cracking and Hydrogen in submerged arc weld metal