Effect of environmental and material factors on SSC property of super 13Cr steel for OCTG.
スポンサーリンク
概要
- 論文の詳細を見る
The susceptibility of pitting and cracking of super 13Cr steels in light sour environment was systematicaly investigated by a notched bent beam test using autoclave. In mild condition such as chloride free solution at 25°C, the steels presents the passive state with no pitting and no cracking. With increase in chloride concentration, corrosion morphology changes from passive state into either pitting or general corrosion allowing hydrogen entry into steel so that SSC can occur. In higher temperature condition, passive film also becomes unstable to cause either pitting or general corrosion, however, cracking susceptibility decreases. These events suggest that a principal mechanism of SSC of super 13Cr steel is hydrogen embrittlement in condition that some breakdown of passive film undergoes.The major environmental factors affecting the pitting and cracking susceptibility are H2S partial pressure, temperature and chloride concentratoin, while pH effect is relatively small. The pitting and cracking resistance depends on alloy composition especially Mo content, but hardly influenced by strength of material.
- 石油技術協会の論文
石油技術協会 | 論文
- 地震波シミュレーションが地下構造探査に果たす役割
- インバージョンテクトニクス
- 最近の探鉱プレイへの構造形成モデルの貢献
- 堆積盆地の地史情報に基づく沈降モデルと構造形成--日本海東部と中国北部湾を例にして (第55回石油技術協会総会地質・探鉱部門シンポジウム--堆積盆地評価とその応用)
- 東北裏日本海域における石油の生成と移動の時期 (「石油の生成と移動の時期」シンポジウム特集号)