Cumulative Damage in Low Cycle Fatigue Part 1:Effects of Cycle Ratio in Two Step Test on 60 kg/mm<SUP>2</SUP> High Tensile Steel
スポンサーリンク
概要
- 論文の詳細を見る
This paper describes the two step low cycle fatigue tests on hourglass shaped specimens of a 60 kg/mm<SUP>2</SUP> high strength steel. Strain controlled tension-compression fatigue tests were performed to study the damage processes in low cycle fatigue. The cycle ratio in the first step was varied in five conditions. <BR>It was found that original material of the 60 kg/mm<SUP>2</SUP> high strength steel showed in the general the similar behaviors to the 80 kg/mm<SUP>2</SUP> high strength steels which were studied in the previous report. The relation between longitudinal plastic strain amplitude and crack initiation life for original material indicated the linear relationship in the log-log plot. The materials which were damaged by the first step strain cycling of longitudinal true strain amplitude of 0.05 with the cycle ratio of 0.19, 0.38 and 0.57 on the crack initiation basis, showed the knuckled line relations of ε-N<SUB>c</SUB> curves. The knuckle point was found on the strain level in the first step. The value of index in the Manson-Coffin equation for materials damaged by the first step strain cycling is smaller than that for original material in the case of step-up test. For step-down test little difference was found between the indices for the original and the damaged materials. <BR>The mean value of the usage factor on the crack initiation basis was 0.82 to 1.09, and that on the failure basis was 0.93 to 1.01. Cycle ratio in the first step scarecely affected the static fracture ductility of damaged materials. On the contrary significant decreasing tendency of the cyclic fracture ductility was observed for damaged materials with increasing cycle ratio in the first step as a parameter, where the cyclic fracture ductility was defined as the product of total true strain amplitude and <I>k</I>th power of cycles to crack initiation in the second step. The cyclic fracture ductility for materials tested by step-down method was always higher than that for specimens tested by step-up method.
- 社団法人 日本船舶海洋工学会の論文
社団法人 日本船舶海洋工学会 | 論文
- A Modified Recovery Procedure to Improve the Accuracy of Stress at Central Area of Bilinear Quadrilateral Element
- 船舶操縦運動の学習型フィードフォワード制御方式の実用化に関する研究(III) - 実船実験による風外乱補償制御系の検証 -
- 溶接継手の疲労寿命に及ぼす荷重履歴の影響
- Evaluation of Marine Wave Radar (Part II) - Wave Parameters from Radar Images -
- 船底横桁の座屈強度に関する研究