Tribological Properties of Cr Plated (NbTi)3Sn Superconducting Wire in Liquid Helium.
スポンサーリンク
概要
- 論文の詳細を見る
Superconducting wires in a cable-in-coduit conductor are plated with chromium for reducing AC loss. However, the wire will suffer from fretting motion with a very small slip amplitude by the repeated pulse operation of the coil, which would damage the plated layer. In this paper, tribological properties, i.e., frictional and wear properties, of Cr-plated (NbTi)3SN wire were examined under a crossed-cylinder contact at mainly 4.2K in liquid helium. Coefficient of friction of Cr-plated wire ranged between 0.2 and 0.5, which was lower than that of copper. Wear volume was small at 4.2K, compared with those at 293 and 77K. The significant damage was the plastic deformation of the plated layer in the wear scar at 4.2K. However, the plated layer was broken and separated at the boundary of the wear scar. The cracks propagated from the circumferential cracks existing before the test. The particles formed were rectangular with a length of about 20μm. When the plated layer was broken, the coefficient of friction increased to that higher than unity.
- 公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会)の論文
公益社団法人 低温工学・超電導学会 (旧 社団法人 低温工学協会) | 論文
- Test Results of the SMES Model Coil. Cool-down and Thermal Characteristics.:Cool-down and Thermal Characteristics
- Crystal Growth of Y Based Superconductors on Solidification Processing.
- Refrigeration of pressurized He II using a 3He circulation system. (II). Behavior of the system during the initial cooling and after a pulsed heat generation.:Behavior of the System during the Initial Cooling and after a Pulsed Heat Generation
- Quench simulation analysis of a superconducting coil. II. Simulation.:II. Simulation
- タイトル無し