Production of Charcoal with High Adsorptive Activity from Waste Plywood Panel for Concrete Form.
スポンサーリンク
概要
- 論文の詳細を見る
A large quantity of waste plywood panel for concrete form has recently been generated with progress of construction industry and its effective utilization become a social urgent problem. In this study, the production of charcoal from the waste plywood form and its adsorption characteristics were investigated. The virgin plywood form and the raw plywood material were also examined for reference. The plywood samples was first pulverized as a chip and carbonized at 500-1, 000°C under nitrogen atmosphere using an electric furnace. The yield of the charcoal was slightly decreased with increasing carbonization temperature, being about 30% at 800°C in the same manner as ordinary charcoals. The specific surface area of the charcoal was increased remarkably at the temperature range over 800°C. X-ray diffraction analysis reveals that the partial graphitization proceeded at carbonization temperature range over 800°C, particularly in the case of the waste plywood form. In the experiments of adsorption in aqueous solutions, the charcoal from the waste plywood form was found to have 3-5 times activity in the adsorption of alkaline dye (methylene blue) and acidic dye (orange II) compared to that from the raw plywood material and about 15 times activity in the adsorption of bisphenol A which is one of endocrine disruptors. Chemical analysis shows that the content of metal ions such as Ca<SUB>2+</SUB>, Na<SUB>+</SUB>, K<SUB>+</SUB>, Al<SUB>3+</SUB> and Total-Fe was considerably larger in the charcoal from the waste plywood form than in that from the virgin plywood form and the raw plywood material. Therefore, the partial graphitization of the charcoal assumed to be accelerated by the catalytic action of the metal ions derived from concrete, which leads to the remarkable increase in the hydrophobicity of the charcoal surface, viz, in the adsoptive activity for organic compounds. It was concluded that the charcoal with high adsoptive activity could be produced from the waste plywood form without any additional activation procedures.
- 環境資源工学会の論文
環境資源工学会 | 論文
- 微生物によるバイオマス系廃棄物からの水素生成
- 電気泳動現象を利用したサブミクロンシリカ粒子の分級
- 密閉容器内の沈積物の質量測定および液-液界面の界面位置測定に関する研究
- 講演4 ジグ選別によるASRの分離精製への展開 (環境資源工学会 シンポジウム「リサイクル設計と分離精製技術」 第11回:自動車リサイクル促進のための廃自動車シュレッダーダスト(ASR)の分離精製技術)
- POPs関連物質の加熱挙動に関する研究