Effects of .ALPHA...LAR..RAR...GAMMA. partial transformation on recrystallization after hot deformation in 17%Cr stainless steel.
スポンサーリンク
概要
- 論文の詳細を見る
The isothermal recrystallization behavior of 17% Cr stainless steel at the temperature range from 900 to 1250°C was investigated with a plain compression type hot deformation simulator. Special emphasis was put on the effects of α_??_γ partial transformation on recrystallization, which were studied by varying the amount of γ phase prior to deformation. In the partial transformation region, the effects of transformation on recrystallization were markedly large. When specimens were cooled down from the a single phase region to the α+γ phase region, recrystallization was suppressed by the strain enhanced transformation of α→γ. When specimens were cooled down from the α+γ phase region to the α+carbides phase region, recrystallization was suppressed by the strain enhanced decomposition of γ phase. From the above results, the suppression of recrystallization was attributed to the depletion of recrystallization nucleation sites by the strain enhanced partial transformation.
- The Iron and Steel Institute of Japanの論文
The Iron and Steel Institute of Japan | 論文
- The Evolution of Precipitates in Nb-Ti Microalloyed Steels during Solidification and Post-solidification Cooling
- Short Contribution to the Study of the Washing Effect in Electromagnetic Stirrers for Continuous Casting
- Nitrogen Bearing Martensitic Stainless Steels : Microstructure and Properties
- A Two-dimensional Finite Element Thermomechanical Approach to a Global Stress-Strain Analysis of Steel Continuous Casting
- Transformation Behavior and Microstructures in Ultra-low Carbon Steels