Fundamental Studies on the Mechanization of the Leaf Stripping Operations for Sugar Cane(III). Wearing Characteristics of Leaf Stripping Steel Roll.:Wearing Characteristics of Leaf Stripping Steel Roll
スポンサーリンク
概要
- 論文の詳細を見る
In order to develop a durable steel roll of the drum type leaf-stripping machine for sugar cane, the wearing characteristics of the leaf-stripping steel roll were analyzed. The obtained results are as follows.1) The wear resisting rate at the dry portion of the carburizing and induction hardening STKM-17A steel roll showed higher value as compared with the wet portion. The wear resisting rate was 97.3% at the dry portion, 96.9% at the wet portion under the elapsed time of 800 hours, respectively.2) In case of the setting a limit of the durability to 98.0%, the durable time was about 550 hours at the dry portion, and about 450 hours at the wet portion.3) The height of knurling was 0.26mm at the dry portion and 0.18mm at the wet portion under the elapsed time of 450 hours, respectively.4) The wear resisting rate of the induction hardening SUJ-3 steel roll was 97.5% at the dry portion and 97.2% at the wet portion under the elapsed time of 800 hours, respectively.5) The durable time was about 630 hours at the dry portion and about 520 hours at the wet portion. The height of knurling was 0.35mm at the dry portion and 0.29mm at the wet portion under the elapsed time of 450 hours.6) The wear resisting rate of the carburizing and induction hardening SUJ-3 steel roll was 97.9% at the dry portion, 97.5% at the wet portion under the elapsed time of 800 hours. These rates showed higher value as compared with the induction hardening SUJ-3 steel roll, respectively.7) The durable time was about 750 hours at the dry portion, about 620 hours at the wet portion. The height of knurling was 0.43mm at the dry portion, 0.37mm at the wet portion under the elapsed time of 450 hours, respectively.8) The durable time of the carburizing and induction hardening SUJ-3 steel roll was about 1.4 times longer (the increase of the cane treatment of about 170 ton) as compared with the carburizing and induction hardening STKM-17A steel roll. But, these values should be analyzed under practical field tests.9) The main reason for lower wear resisting rate at the wet portion could be considered that there is effect of the corrosion on the steel roll surface. In order that the results, cane juice should be eliminated from the steel roll surface after the practical operation.
- 日本農作業学会の論文
日本農作業学会 | 論文
- 日本とオランダにおけるチューリップ球根生産者の生活時間構成の比較--大規模経営における農繁期の調査事例
- 不織布マルチングによる水稲直播・有機栽培--代かき時期と基肥施用時期の影響
- ガソリンエンジン排気ガス中のエチレンが施設内作物の落花・落蕾に及ぼす影響
- ハイパースペクトル画像解析によるカバークロップ圃場の構成草種および草量の空間分布推定
- 乗用型トラクタによるリバーシブルプラウ作業の習熟過程に関する人間工学的研究