In this study, two types of porous zirconia and dense zirconia were used. The flexural strength of non-layered zirconia specimens and those of the layered zirconia specimens with veneering porcelain were examined. Furthermore, the shear bond strength of veneering porcelain to zirconia was examined. The flexural strength of the non-layered specimens was 1,220 MPa for dense zirconia and 220 to 306 MPa for porous zirconia. The flexural strength of the layered specimens was 360 MPa for dense zirconia and 132 to 156 MPa for porous zirconia, when a load was applied to the porcelain side. The shear bond strength of porcelain veneered to dense zirconia was 27.4 MPa and that of porcelain veneered to porous zirconia was 33.6 to 35.1 MPa. This suggests that the veneering porcelain bonded strongly to porous zirconia although porous zirconia has a lower flexural strength than dense zirconia.
- 日本歯科理工学会の論文
日本歯科理工学会 | 論文
- A-33 レイヤリングテクニックとプレスオンテクニックにより製作したジルコニアクラウン(セラミックス,一般講演(口頭発表),第54回日本歯科理工学会学術講演会)
- B-4 IPS Empress 2コア材の繰り返し焼成が接着強さに与える影響(接着2, 第49回日本歯科理工学会学術講演会)
- IPS Empress 2ガラスセラミックスの最適な表面処理条件 : 第1報 各種酸処理が曲げ強さに与える影響(臨床応用, 平成17年度秋期 (長崎) 第46回日本歯科理工学会学術講演会)
- P-95 骨芽細胞様細胞によるジルコニアとチタンの生体適合性の比較評価(生体用セラミックス2,一般講演(ポスター発表),第54回日本歯科理工学会学術講演会)
- A-13 シリコン種含有ポリ乳酸系ハイブリッド膜の生体適合性評価(生体反応2,一般講演(口頭発表),第53回日本歯科理工学会学術講演会)