Permeability Measurements of Magnetic Thin Film with Microstrip Probe

概要

論文の詳細を見る
A highly sensitive and broadband method of obtaining thin film permeability without sample-size limitations was developed based on the change in high-frequency impedance due to the skin effect. A microstrip probe with impedance matching of 50 Ω was fabricated, and placed in proximity to a magnetic thin film. The permeability was optimized with the Newton-Raphson method. The permeability of CoFeB film (45 mm × 25 mm and 0.5 μm in thickness) and that of FeCoB/Ru film (50 mm × 40 mm and 0.2 μm in thickness) were evaluated using a permeameter. The measured values were in rough agreement with theoretical values based on the Landau-Lifshitz-Gilbert equation and eddy current generation up to 30 GHz. The proposed method offers promise for measuring the permeability of wafer-sized samples in line because it is not restricted by size limitations.
公益社団法人日本磁気学会の論文