無電解Ni-Bめっきの初期析出におよぼす浴中化学種の影響
スポンサーリンク
概要
- 論文の詳細を見る
Important factors for fabricating thinner and more uniform films by electroless Ni-B plating using dimethylamine borane (DMAB) as the reducing agent were discussed. The number density of initial deposits was pointed out as the important factor for fabrication of thinner and more uniform films. Transmission electron microscope observations were performed for initial deposits plated from baths of different pH. The number density was lower in deposits plated from pH 9-10 than in those plated from pH 6-8. Dimethylamine produced through an oxidation reaction of a reducing agent (DMAB) prevents the initial deposition. Such a lower number density appeared in pH 9-10.Nickel citrate - ammonia complex was formed under ammoniacal conditions. The nickel citrate - ammonia complex contributed to the increase in the number density of grains. It was possible to eliminate deposition prevention through the appropriate selection of nickel complexes. Results show that the initial deposition with higher number density of grains was achieved at all pH of Ni-B plating baths.
- 一般社団法人 表面技術協会の論文
一般社団法人 表面技術協会 | 論文
- ニオブアノード酸化皮膜の成長挙動と微細構造制御
- UV照射を用いた樹脂表面改質におけるめっき密着メカニズム
- ホウ酸代替物質を使用したスルファミン酸ニッケル浴から得られためっき皮膜物性とその応用
- 平滑な樹脂基板上へのメタライゼーション
- テトラエチルシランを用いたSi(111)基板上における3C-SiCのエピタキシャル成長とヘテロ界面におけるボイドの抑制