電析Pd-Ni-P金属ガラスの熱処理による結晶化挙動
スポンサーリンク
概要
- 論文の詳細を見る
Crystallization behavior of electrodeposited Pd-Ni-P metallic glass films in the supercooled liquid region was investigated. The Pd40Ni40P20, which has the highest glass formability, and other metallic glass Pd44Ni39P17 and Pd41Ni42P17 were prepared. The crystallization temperature (Tx) of Pd44Ni39P17 and Pd41Ni42P17 were lower than that of Pd40Ni40P20 by differential scanning calorimetry (DSC) analysis. X-ray diffractometry (XRD) patterns show that all samples were crystallized after isothermal annealing below Tx. The Pd5P2 and Ni3P were observed using XRD analysis after annealing of Pd40Ni40P20 and Pd44Ni39P17 at 603 K for 60 min and 30 min, respectively. Furthermore, in Pd44Ni39P17, the Pd2Ni2P was observed after annealing at 603 K for 120 min.
- 一般社団法人 表面技術協会の論文