Influence of Basicity and TiO2 Content on the Precipitation Behavior of the Ti-bearing Blast Furnace Slags

スポンサーリンク

概要

• 論文の詳細を見る

• The present paper investigated the influence of basicity and TiO2 content on the crystallization behavior of the Ti-bearing blast furnace slag (Ti–BF slag). Single Hot Thermocouple Technique (SHTT) was applied to construct the Time-Temperature-Transformation (TTT) diagrams. Scanning Electron Microscope equipped with Energy-Dispersive X-ray spectroscope (SEM-EDX) and X-Ray Diffraction (XRD) were employed to observe the morphology and determine the crystalline phase of the Ti-enriched crystals. It was found that rutile was formed as the Ti-enriched phase when the basicity of the sample was lower than 0.6, and perovskite appeared as the Ti-enriched phase with an increasing basicity to 1.0. It was also noticed that the addition of TiO2 could decrease the incubation time in the TTT diagram of the samples. The kinetics of the formation of Ti-enriched crystals, rutile and perovskite, was studied, and the mechanism of crystallization and growth was further discussed. The results indicated that the crystallization of rutile was one-dimensional interface-controlled growth, and the nucleation rate varied with the holding time at different TiO2 content. While the precipitation behavior of perovskite was three-dimensional diffusion-controlled growth, and its nucleation rate decreased with the holding time.

• The Iron and Steel Institute of Japanの論文

著者

• Wang Wanlin

  School Of Metallurgical Science And Engineering Central South University

• Li Jing

  Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University

• Zhang Zuotai

  Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University

• Liu Lili

  Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University

• Wang Xidong

  Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University

関連論文

• Influence of TiO_2 on the Viscous Behavior of Calcium Silicate Melts Containing 17 mass% Al_2O_3 and 10 mass% MgO
• Radiative Heat Transfer Behavior of Mold Fluxes for Casting Low and Medium Carbon Steels
• A Kinetic Study of the Effect of Na2O on the Crystallization Behavior of Mold Fluxes for Casting Medium Carbon Steel
• Effect of Na2O and B2O3 on Heat Transfer Behavior of Low Fluorine Mold Flux for Casting Medium Carbon Steels
• Influence of Basicity and TiO2 Content on the Precipitation Behavior of the Ti-bearing Blast Furnace Slags

スポンサーリンク