Weldability of A6082 with Nd-YAG laser was investigated to explain the advantages over the conventional MIG process. It is concluded that rapid cooling rate in HAZ contributes to increasing joint strength and improvement durability against liquation cracking in HAZ during Nd-YAG laser welding. This is why rapid cooling rate is enough to prevent crossing the C-curve for precipitation of β´and small volume of weld metal is enough to reduce shrinkage strain during solidification. And the joint strength increased with an increase of manganese content in the base metal, but by contraries the minimum hardness in HAZ where the fracture occuued in the tensile test decreased. This may be attributed to the prevention of intercrystalline embrittlement due to the addition of managanese in case of Al-Mg-Si series alloys with excessive Si content.
- 一般社団法人 軽金属溶接協会の論文
一般社団法人 軽金属溶接協会 | 論文
- AZ31マグネシウム合金の摩擦撹拌点接合時の塑性流動および継手強度に及ぼすツール形状の影響
- プラズマアークによるアルミニウム厚板のキーホール溶接の数値シミュレーション
- 5052Al及び6063Al合金のパルス通電接合部の熱処理による改善
- ブレージングシートの外部耐食性に及ぼす心材Cu量、ろう材Zn量および板厚の影響
- 半溶融状態のはんだを用いた超音波はんだ付によるアルミニウム継手の強度と耐食性