回折X線プロファイル解析を用いた引張負荷による鋼の微視構造変化と力学特性の評価

スポンサーリンク

概要

• 論文の詳細を見る

• X-ray line profile analysis, modified Williamson-Hall method/modified Warren-Averbach method, was carried out to measure microscopic parameters such as dislocation density and crystallite size of S45C steel with tensile loading after released. As the result, X-ray line profiles were broadened after yield process due to convolution of increase of dislocation density and refinement of crystallite size. Correlations between microscopic parameters and macroscopic parameters such as flow stress, plastic strain, and Vickers hardness were also discussed. Then followings were clarified, relationship between flow stress and dislocation density that measured by X-ray diffraction agrees with conventional relationship,τ = τ0 + κμbρ1/2, which had been obtained by TEM observation and etch-pit technique; plastic strain after plateau region has relationship to dislocation density, ρ = ρ0 + Dεpm, which means it is able to measure plastic strain by X-ray diffraction; Vickers hardness relates to square root of dislocation density as linear function.

著者

• 熊谷 正芳

  Tokyo city university, Department of Mechanical Systems Engineering

• 菊地 拓哉

  Tokyo city university, Graduate school of engineering

• 今福 宗行

  Tokyo city university, Department of Mechanical Systems Engineering

• 大谷 眞一

  Tokyo city university, Department of Mechanical Systems Engineering

関連論文

• 回折X線プロファイル解析を用いた引張負荷による鋼の微視構造変化と力学特性の評価

スポンサーリンク