An empirical model has been developed based on optical basicity to calculate the sulfide capacity of metallurgical molten slag. The model estimated sulfide capacities agree well with the experimental data for CaO–MgO–FeO–MnO–TiO2–Al2O3– SiO2–CaF2 multicomponent slags. It is found that the abilities of increasing sulfide capacity in MO–SiO2 (M=Ca, Mg, Fe and Mn) melts follow the order: MnO>FeO>CaO>MgO. Also, substitution of CaO for CaF2 decreases the sulfide capacity and substitution of TiO2 for SiO2 increases the sulfide capacity.
著者
-
PAL Uday
Department of Manufacturing Engineering, Boston University
-
Chou Kuo-chih
State Key Laboratory Of Advanced Metallurgy University Of Science And Technology Beijing
-
Zhang Guo-hua
State Key Laboratory Of Advanced Metallurgy University Of Science And Technology Beijing
-
Pal Uday
Department of Mechanical Engineering and the Division of Materials Science and Engineering, Boston University
関連論文
- Rate of Reduction of Ferric and Ferrous Oxide from Calcia-Silica-Alumina Slag by Carbon in Luquid Iron
- Incorporation of Sulfur in an Optimized Ladle Steelmaking Slag
- Incorporation of Chlorine in a Secondary Steelmaking Slag Based on the CaO-Al_2O_3-SiO_2 System
- Modelling Viscosities of CaO-MgO-Al_2O_3-SiO_2 Molten Slags
- Modelling Viscosities of CaO–MgO–Al2O3–SiO2 Molten Slags
- Interfacial Rate of CO2–CO Reaction with the Solid Iron and Iron Oxide by Isotope Exchange Technique at 1273 K
- Estimation of Sulfide Capacities of Multicomponent Slags using Optical Basicity
- Selective Chlorination Reaction of Cu2O and FeO Mixture by CaCl2
- Influence of Al2O3/SiO2 Ratio on Viscosities of CaO–Al2O3–SiO2 Melt
- Removal of FeO during Foaming of CaO-Al2O3-SiO2-FeO Slags by Low Carbon-Iron Melts.
- Laboratory Scale Refining Studies on Low Carbon Aluminum Killed Steels Using Synthetic Fluxes.
- Reduction Kinetics of FeTiO3 Powder by Hydrogen
- Interfacial Rate of CO_2-CO Reaction with the Solid Iron and Iron Oxide by Isotope Exchange Technique at 1273 K
- Selective Chlorination Reaction of Cu_2O and FeO Mixture by CaCl_2
- Reduction Kinetics of FeTiO_3 Powder by Hydrogen
- Influence of Al_2O_3/SiO_2 Ratio on Viscosities of CaO-Al_2O_3-SiO_2 Melt