Initial Fragmentation Process of Aluminum-Alloy Plate by Hypervelocity Spherical-Projectile Impact
スポンサーリンク
概要
- 論文の詳細を見る
In order to characterize the dynamic fracture of Al plate caused by impact with a hypervelocity spherical Al projectile, experiments were performed using a mini two-stage light gas gun. Spherical Al-alloy projectiles with a diameter of 2.1 mm were accelerated to 3.5 km/s and allowed to impact with Al targets under normal impact conditions. The dynamic deformation and fragmentation of the target were observed using a high-speed digital framing camera. The digital images revealed local displacement (bulging) of the target surface, and fragmentation resulting from the large displacement was also observed. Additionally, it was found that the motion of the target fragments was strongly correlated with the bulge growth process. The sequence of dynamic processes from bulging to fragmentation is discussed.
著者
関連論文
- 放電合成法における新しいアミノ酸生成機構の提案
- 高温プラズマMPDアークジェットによる有機化合物の合成
- 電熱爆発粉体溶射による複合セラミックコーティング
- 電熱爆発粉体溶射法による炭化硼素皮膜の合成
- 電熱爆発粉体溶射法による炭化硼素皮膜の化学合成
- 電熱爆発粉体溶射法によるZr-O-B系複合物 / Ni-20%Cr傾斜構造皮膜の形成
- 反応性溶射によるZr-O-B系セラミックス/Ni-20%Cr傾斜皮膜の合成
- 3p-RD-1 金属蒸気を含むプラズマチャネルのレーザー始動実験IV
- 12a-DH-4 金属蒸気を含むプラズマチャネルのレーザー始動実験III
- 29a-B-6 金属蒸気を含むプラズマチャンネルのレーザー始動実験 II
- 3a-CD-5 金属蒸氣を含むプラズマ・チャネルのレーザー始動実験
- 衝撃波の干渉を利用した新しい衝撃合成方法の開発と B-C-N 系化合物合成の試み
- 電熱爆発粉体溶射法によるZrB_2-ZrO_2複合皮膜の化学合成
- 高速・高密度セラミックジェットによる溶射複合コーティングの探索
- 最近の溶射研究
- 電熱爆発粉体溶射法と皮膜の性状
- 高速セラミックジェットによる高融点セラミックス溶射コーティング
- 高速セラミックジェットの発生とホウ化物コーティングの形成
- 導電性粉体用電熱爆発溶射法の開発 : 高融点セラミックスの溶射例
- 4p-K-3 光電離プラズマのパルスイオン源への応用
- 2a-F-13 プラズマチャネルの始動と形成
- 固相破片デブリスの損傷能力の見積もり
- 308 MPDアークジェットによるアミノ酸の短時間大量合成(セッション3)
- Initial Fragmentation Process of Aluminum-Alloy Plate by Hypervelocity Spherical-Projectile Impact
- 27aXZA-7 Rb被覆Si表面におけるSHG共鳴増大の温度効果に対する分光学的研究(27aXZA 表面界面ダイナミクス,領域9(表面・界面,結晶成長))
- 28pJA-3 レーザー第2高調波発生法を用いたRb飽和被覆Si(100)表面におけるRb原子拡散と表面構造の考察(表面界面構造,領域9(表面・界面,結晶成長))