Nanostructured Titanium Oxide Fabricated via Block Copolymer Template

スポンサーリンク

概要

• 論文の詳細を見る

• Titanium tetrachloride vapor was selectively introduced into hexagonally arranged PEO cylinders in PEOm-b-PMA(Az)n ((m, n)=(272, 116), (272, 94), and (114, 67)) thin films by simply exposing the films to the vapor in a glass vessel. TEM images of PEOm-b-PMA(Az)n thin films with m=272 and 114 after the exposure showed hexagonally arranged dark spots with 14-nm diameter and 38-nm distance, and 10-nm diameter and 20-nm distance, respectively. FTIR measurement indicated a change in the peak shape at stretching vibration of C-O-C in the PEO chain as titanium tetrachloride was introduced. The film weight during the vapor process was increased in QCM measurement. XPS analysis was carried out for the films before and after hydrolysis with water vapor. It was found that titanium oxide with some different oxidation states existed in the hydrolysis treatment. FESEM revealed that calcination of the hydrolyzed film gave titanium oxide nanowires with about 10-nm diameter. XRD pattern of the calcined film suggested that the process demonstrated here generated the titanium oxide nanowires consisting of polymorph mixture with brookite, rutile, and anatase.

著者

• ITO Kaori

  Division for Animal Resources and Development, Life Science Research Center, University of Toyama

• Iyoda Tomokazu

  Division Of Integrated Molecular Engineering Chemical Resources Laboratory Tokyo Institute Of Technology

• Watanabe Ryoko

  Division of Integrated Molecular Engineering, Chemical Resources Laboratory, Tokyo Institute of Technology, Yokohama 226-8503, Japan

• ITO Kaori

  Division of Integrated Molecular Engineering, Chemical Resources Laboratory, Tokyo Institute of Technology

関連論文

• 国動協および公私動協において動物実験に用いられたサルおよびブタのHEV感染調査
• Synthesis of Poly(isothianaphthene) by Photopolymerization of 1,3-Dihydroisothianaphthene
• Preparation of Polyviologen-modified TiO_2 by Photocatalytic Polymerization of Bis(4-cyano-1-pyridinio )- P-xylene Dibromide
• Nanohole Arrays Fabricated on Gold Surfaces by Total Wet Nanopatterning through Block Copolymer Masks
• Perpendicularly Oriented Cylinder Nanostructure of Liquid Crystalline Block Copolymer Film on Si Substrate with Various Surface Wettability
• Nanodimple Arrays Fabricated on SiO2 Surfaces by Wet Etching through Block Copolymer Thin Films
• Nanostructured Titanium Oxide Fabricated via Block Copolymer Template

スポンサーリンク