SOFC-SOEC Characteristics of an Intermediate-temperature Micro-tubular Ceramic Reactor Using Ag for Current Collecting

スポンサーリンク

概要

• 論文の詳細を見る

• Ni-based electrode-supported cells with a Sc2O3-stabilized ZrO2 electrolyte have been evaluated as solid oxide fuel cells (SOFCs) and solid oxide electrolysis cells (SOECs) in intermediate-temperature operation. Using a Ag current collector, a power density of 1.68 W cm－2 at 2.87 A cm－2 and an electrolysis voltage of 1.42 V at 0.57 A cm－2 were obtained at 650°C. The current efficiency in steam electrolysis was almost 100%. This suggests that the high performance is related to decreases in current collector resistance and polarization of the air electrode, due to the formation of Ag current collecting paths on the air electrode. During a 450 h durability measurement in SOEC mode, a degradation rate of 0.056 mV h－1 was observed. Impedance measurements showed the polarization of the steam electrode increased, while the polarization of the air electrode and ohmic resistance showed no change, after the long-term SOEC operation.

著者

• WANG Zhenwei

  Materials Science Research Laboratory, Central Research Institute of Electric Power Industry

• MORI Masashi

  Materials Science Research Laboratory, Central Research Institute of Electric Power Industry

関連論文

• Investigation of Current Leakage of Micro-tubular SOFCs with a Ceria Membrane for Low-intermediate Temperature Power-generation Applications
• SOFC-SOEC Characteristics of an Intermediate-temperature Micro-tubular Ceramic Reactor Using Ag for Current Collecting

スポンサーリンク