Au alloys have great potentialities as solder joints of electronic packaging. However, studies on mechanical properties of Au solders, especially on creep properties, are very limited. Mechanical properties of Au-20Sn and Au-12Ge were measured by indentation tests ranging between nano and macro scales. First, macro indentation creep tests were carried out at various temperatures, i.e. 295K, 323K, 373K, 398K and 423K. It was found that the indentation creep deformation was observed at room temperature for Au-20Sn, while above 373K for Au-12Ge. Second, the indentation creep properties were measured for <I>ζ</I> and <I>δ</I> phases of Au-20Sn using a nano-indentation testing machine in order to investigate the influences of microstructure on the creep properties. Finally, we evaluated anisotropy of textured microstructure of Au-12Ge, where the dent shapes were distorted. This behavior was attributed to the three dimensional configurations, namely pile-up and sink-in. Based on the results of nano-indentation tests, numerical model for the microstructure of Au-12Ge was established and the mechanisms of the pile-up and sink-in were discussed.
- 日本材料学会の論文
著者
関連論文
- インデンテーション法によるWC-Co溶射材の静的および疲労強度特性評価
- 構造最適設計における設計条件と設計手法の明確化のための系統的方法論
- き裂先端部近傍の変位場を用いた混合モード応力拡大係数評価法
- ポリプロピレンのインデンテーション法によるクリープ特性評価
- 2016 ポリプロピレンのインデンテーション法によるクリープ特性評価(S16-1 特性評価,S16 インデンテーションの物理と応用)
- 接触負荷を受けるダイヤモンドライクカーボン膜の破壊メカニズム
- 2015 インデンテーション法におけるDLC膜の破壊メカニズム(S16-1 特性評価,S16 インデンテーションの物理と応用)
- 押込み試験中のAE・腐食電位揺動同時計測による気相合成ダイヤモンド膜の破壊強さ測定
- AEと腐食電位揺動解析によるSUS304鋼の塩化物応力腐食割れプロセスの観察
- 2823 AEと腐食電位揺動を用いた二相ステンレス鋼の環境助長割れのメカニズム(S37-1 非破壊評価とモニタリング(1),S37 非破壊評価とモニタリング)