The character of acid sites on the gypsum surface.
スポンサーリンク
概要
- 論文の詳細を見る
The maximum value in the number of acid sites per unit of surface area of the gypsum formed in the reaction between Ca(NO<SUB>3</SUB>)<SUB>2</SUB> and H<SUB>2</SUB>SO<SUB>4</SUB> was observed at the heat-treatment temperature of 200 °C, corresponding to the dehydration temperature for the change from its hemihydrate form to soluble anhydrite. The IR-absorption spectra of the gypsum showed no bands assignable to isolated OH groups or Ca–OH species. The IR spectra of the pyridine adsorbed on the gypsum showed only the bands due to Lewis-acid sites. The gypsum heat-treated at temperatures lower than 500 °C showed catalytic activities for the double-bond isomerization of 1-butene. The <I>cis-/trans</I>- ratio of 2-butene was 2–2.5, showing that the catalytic activity was due to Lewis acid, not to Brönsted acid. The isomerization of cyclopropane to propene was scarcely promoted by the gypsum at 250 °C. This fact is another indication of the absence of Brönsted acid sites on the heat-treated gypsum. Most of the weak Lewis acid sites (<I>H</I><SUB>0</SUB>≤+4.8) were ascribable to exposed Ca<SUP>2+</SUP> ions surrounded by monodentate sulfate ions on the surface of metastable anhydrite III-CaSO<SUB>4</SUB>.
- 公益社団法人 日本化学会の論文
著者
-
Okazaki Susumu
Depariment Of Physics Faculty Of Science Okayama University
-
Yamazaki Mituo
Department of Industrial Chemistry, Faculty of Engineering, Ibaraki University
関連論文
- Preparation of C_Microcrystals Using High-Temperature and High-Pressure Liquid Crystallization Method
- Spontaneous Fluctuations and Lifepath in Silicon
- A Neutron Diffraction Study of Structure of Molten Thallium(1) Chloride (特集 New Trends in Molten Salt Chemistry and Electrochemistry)
- Density Fluctuation and Hydrogen-Bonded Clusters in Supercritical Water. A molecular Dynamics Analysis Using a Polarizable Potential Model
- Noise in Germanium
- Double Injection in Trap-Free Silicon at High Operating Points
- Carrier Density and Mobility Obtained from Space-Charge-Limited Current in P-Type Silicon
- Properties of Intersurface in Au-Insulator-CdS Measured by Capacitance Method
- Experimental Investigation of Double Injection in p-Type Silicon
- The adsorption of basic .ALPHA.-amino acids in an aqueous solution by titanium(IV) oxide.
- The effect of phosphoric acid treatment on the catalytic property of niobic acid.
- The character of acid sites on the gypsum surface.
- Nb2O5 supported on TiO2. Catalytic activity for reduction of NO with NH3.