Temperature-programmed desorption of ammonia on zeolites. Influence of the experimental conditions on the acidity measurement.
スポンサーリンク
概要
- 論文の詳細を見る
The Influence of the experimental conditions of the TPD (Temperature-Programmed Desorption) of ammonia on the measurement of acidity of mordenites and Y zeolites was studied. The results were applicable to the measurements of the strength and the number of acid sites of zeolites. For contact times of the carrier gas from 10<SUP>−2</SUP> to 10<SUP>−6</SUP> g min ml<SUP>−1</SUP> defined as <I>W</I>/F (<I>W</I>, sample weight; F, flow rate of the carrier gas), the peak maximum temperature was related to the parameter (<I>W</I>/F). The relationship was explained on the basis of a theoretical equation derived by Cvetanovic and Amenomiya under the conditions of readsorption. Ammonia is readsorbed on zeolites under these conditions, and one has to use the experimental conditions of the same contact time in order to evaluate the acid strength of zeolite from the peak maximum temperature. On the other hand, the ratio of intensity of low temperature peak (1-peak) to that of the high temperature peak (h-peak) increased with increasing the contact time of the carrier gas. This relation suggested that the 1-peak intensity depended upon the degree of evacuation of the weakly-held ammonia. The 1-peak is ascribable to very weakly or physically adsorbed ammonia on zeolites, and only the h-peak has to be accounted for to measure the number of acid sites.
著者
-
Niwa Miki
Department Of Chemistry And Biotechnology Graduate School Of Engineering Tottori University
-
Iwamoto Masakazu
Department of industrial chemistry,Faculty of Engineering,Miyazaki,University
-
Segawa Koh-ichi
Department of Chemistry, Faculty of Science and Technology, Sophia University
関連論文
- Periodic DFT Calculation of the Energy of Ammonia Adsorption on Zeolite Bronsted Acid Sites to Support the Ammonia IRMS-TPD Experiment
- A New SOx Deactivation-Free NOx Reduction System Using Rh/Alumina and Periodical Rich and Lean Conditions
- Active and Reusable Catalyst in the Friedel-Crafts Alkylation Derived from a Heteropoly Acid
- Selective Catalytic Reduction of NO by Methane over Pd Loaded on Heteropolyacids/SiO_2 at Low Temperature
- Studies on the Formation and Structure of Highly Dispersed PdO Interacted with Bronsted Acid Sites of Zeolite by EXAFS
- Shape-Selective Adsorption of Substituted Benzaldehyde Isomers by a Molecular Sieving Silica Overlayer Prepared by the Chemical Vapor Deposition Method Using Organic Template on Tin Oxide
- Formation of Selective Adsorption Cavity by Chemical Vapor Deposition of Molecular Sieving Silica Overlayer on Alumina using Molecular Template in the Presence of Acetic Acid
- A Continuous-Flow Method for Chemical Vapor Deposition of Tetramethoxysilane on γ-Alumina to Prepare Silica Monolayer Solid Acid Catalyst
- Spontaneous Dispersion of PdO onto Acid Sites of Zeolites Studied by in situ DXAFS
- Enhancement of Tolerance to the Humidity by Chemical Vapor Deposition of Silicon Alkoxide on Pd-Mordenite Catalyst in the Reaction of NO, Methane and Oxygen
- Quantitative Measurements of Bronsted Acidity of Zeolites by Ammonia IRMS-TPD Method and Density Functional Calculation
- Distribution of Acid Sites in Mordenite
- Improvement of the Catalytic Performance of Pd/WO_3/ZrO_2 in the Selective NO-CH_4-O_2 Reaction by the Addition of Water Vapor
- Generation and Identification of Strong Acid Sites in AIMCM-41 Prepared by Gel Equilibrium Adjustment Method
- Studies on the Structure and Acid Properties of GaMCM-41 Mesoporous Molecular Sieve
- Molecular-Sieving Gas Sensor Prepared by Chemical Vapor Deposition of Silica on Tin Oxide Using an Organic Template
- Layered Nb_2O_5-WO_x Sheet Catalyst Composed of Nanofibers That Are Active in Friedel-Crafts Reactions
- Enhancement in Cracking Activity of USY Zeolites Treated with Ammonium Nitrate Solution
- Removal of nitrogen monoxide from exhaust gases through catalytic decomposition
- Temperature-programmed desorption of ammonia on zeolites. Influence of the experimental conditions on the acidity measurement.
- Photoregulated ion-binding to azobenzene-linked ethylenediamines and iminodiacetic acids.
- Enhancement of catalytic activity of copper ion-exchanged Y type zeolites for the decomposition of nitrogn monoxide.
- New syntheses and physical properties of p-alkylcalix(n)arenes.
- Hexacarbonylmolybdenum(0)-catalyzed reaction of allylic carbonates with arylsulfonyl-stabilized carbanions.
- ESR spectra of nitric oxide adsorbed on ZrO2, CeO2, and ThO2.
- Quantitative interpretation of infrared diffuse reflectance spectra over whole concentration range.
- Titanium oxide-supported carbonylmolybdenum catalyst in liquid phase: Application to allylic alkylation of methyl p-tolylsulfonylacetate.
- A magnetic resonance study of the Fe2O3/Al2O3 catalyst in a CO-N2O reaction.