非対称正弦波による金の電析
スポンサーリンク
概要
- 論文の詳細を見る
The effects of asymmetric sine-wave current plating on gold deposition have been studied using electrographic tests for porosity and accelerated environment tests. Comparison of the porosity of the deposit with that of a plate deposited under DC current indicated that an asymmetric sine-wave decreased porosity by more than 50%. A salt spray test showed that salt water resistance was improved. Frequencies of 1kHz or less were effective in decreasing porosity and improving resistance, the anodic current of the sine-wave increased the porosity and enlarged the crystal size of the deposits. The implications of these observations relating to the porosity-decreasing mechanism are discussed and compared to those of pulsed current plating.