YAGレーザによる照射部の溶込み状態の評価に関する研究（第２報，照射条件によるAE信号の特徴と溶込み状態の関係）
スポンサーリンク
概要
- 論文の詳細を見る
The laser welding methods are widely used for manufacturing the products that the high quality welding conditions are required. Therefore, the establishment of the evaluation method for the melting conditions is desired. In the previous paper, the method by using the features of detected AE signals, when the irradiation energy was changed at the pulse width, was proposed. The results showed the following: (1) The frequency range of the signal of melting is near 300 kHz. (2) The correlation coefficients of the regression equations that evaluate the melting conditions from the AE energy of transversal wave components showed the high value. (3) The high correlations were recognized with the equations that evaluate the conditions by the led largest Lyapnov exponents from the wavelet transform results of the longitudinal wave component. However, it was proven that the frequency range of the thermal shock wave overlaps to the range of the melting, when the temperature rise rate lowers with the decrease of the lamp input voltage. Therefore, the evaluation method in the previous paper is not able to use in case of the evaluation of the melting conditions under the condition for changing the irradiation energy at the voltage. The method for evaluating the melting conditions, when the irradiation energy is changed by the voltage and the pulse width, is proposed in this paper. Concretely, the detected signals in the range (i.e. after 2 ms from the irradiation completion) that the influence of the thermal shock wave fades out, and the temperature of the irradiation part keeps the over melting point are analyzed with chaos and wavelet transform analysis method. The summaries of the result in this study are like the following. The correlation coefficients of the regression equations that evaluate the melting conditions from AE parameters showed the high value. One of the parameters is the correlation dimension Cd of transversal wave component, and the rest are the largest Lyapnov exponent LLy and the correlation dimension Cd of the time fluctuation waveform on the energy rate of the wavelet coefficient of longitudinal wave component. From the above results, it was shown to be possible that the melting conditions can be evaluated with the proposed method in this study, when the irradiation energy is changed by the lamp input voltage and the pulse width.
著者
関連論文
- 2235 超音波法を用いた応力測定に関する基礎的研究 : 周波数解析の適用(S15-3 実験力学と材料評価(3),S15 実験力学と材料評価)
- 2547 YAGレーザによる溶接部の評価に関する研究 : AE法による溶込み状態の評価(S26 溶接・接合,S26 溶接・接合の動向とその展開)
- 2534 スマート構造・材料に関する基礎的研究 : き裂の進展抑制と修復について(J10-8 き裂治癒,J10 知的材料・構造システム)
- 729 赤外線サーモグラフィによる内部欠陥の3次元形状評価に関する基礎的研究 : 欠陥の厚さの検討(GS-3 欠陥評価,研究発表講演)
- 713 AE法によるMIM加工材料の破壊特性評価(GS-3,4 疲労特性,研究発表講演)
- 705 AE法によるレーザ溶接部の溶込みに関する評価(GS-3 材料計測,研究発表講演)
- 704 AE法による摩耗形態の評価 : シビア・マイルド摩耗遷移とAE波形(GS-3 材料計測,研究発表講演)
- 205 超音波法を用いた金属材料のギガサイクル疲労の損傷評価に関する研究(OS-1 疲労破壊の評価)
- 215 応力誘起マルテンサイト変態の挙動による形状記憶劣化に関する研究 : AE法と分子動力学法の適用(OS-1 無機材料・形状記憶合金の評価)
- AE信号のウェーブレット変換によるFRP積層板の曲げ疲労損傷評価 : フラクタル次元とニューラルネットワークの適用
- 808 FBGによるAE計測に関する基礎的研究 : CFRP積層板への適用(GS-3 計測・検査(1))
- 809 キャビテーション壊食によるTiNセラミックス皮膜の損傷評価に関する研究 : FBGによる損傷検出(GS-3 計測・検査(1))
- YAGレーザによる照射部の溶込み状態の評価に関する研究（第２報，照射条件によるAE信号の特徴と溶込み状態の関係）
- 515 ナノ材料の破壊特性評価に関する基礎的研究 : MD法とAE法の適用(GS-1 ナノ材料・ナノ構造体,研究発表講演)
- 815 赤外線サーモグラフィによる内部欠陥の評価に関する基礎的研究 : 3次元形状の認識(GS-3 可視化計測)
- 226 鋳鋼に生じる白色層の生成状態の評価に関する基礎的研究 : 非線形デジタルフィルタを用いたAE信号の処理結果について(GS-3 計測・検査(4))
- 224 AE法による鋳鋼のき裂進展状態の把握に関する研究 : 白色層の発生状態の違いによる比較(GS-3 計測・検査(3))
- 223 AE法によるFRP積層板の劣化状態の評価に関する研究 : 紫外線劣化と吸水劣化の影響(GS-3 計測・検査(3))
- 222 超音波法を用いた表面開口き裂の深さ測定に関する研究 : 粒子分散複合材料への適用(GS-3 計測・検査(3))
- 207 レイリー波のwavelet変換結果に基づく残留応力分布の評価に関する基礎的研究(GS-3 計測・検査(2))
- 706 AE法による焼入れ状態の評価に関する研究 : YAGレーザによる焼入れの場合(OS7-2 非破壊評価と構造モニタリング)
- 707 ひずみ時効能を付与した新アルミニウム合金の超高サイクル疲労強度特性(高サイクル疲労特性,疲労損傷観察ならびに強度評価,オーガナイスドセッション1)