マグネシア・クリンカーにおける酸化鐵の鑛化作用について (その2)
スポンサーリンク
概要
- 論文の詳細を見る
The microstructure of the magnesia clinker, which was obtained from the light burned magnesia or chemical pure magnesia mixed with 0-10% Fe2O3 as mineralizer and fired 1300-1600°C in 3 hours, was studied.Fe2O3 is as well effective to sintering of magnesia clinker as to developement of periclase crystal, and it is found that Fe2O3 is uniformly distributed within the periclase grain.The periclase crystal is effectively developed when CaO, Fe2O3 content, firing temperature, firing time are increased and ignition loss of a raw magnesia is decreased.Especially, in the case of raw magnesia which containing CaO, the periclase crystal was very large and shows a characteristic structure like a hive.Microstructure of magnesia clinker, such as a sort of periclase crystal, distributed state of anisotropic substance, quantity of a silicate matrix and air void, produced compound, must be dependent chiefly on chemical composition and mutual proportion of CaO, Fe2O3 and SiO2 in the mixture.
- 社団法人 日本セラミックス協会の論文
著者
関連論文
- マグネシウムクロメイトの熱分解
- 10.酸化クロム(III)の焼結と表面活性(研究発表講演要旨)
- CaZrO_3-Cr_2O_3 系反応
- 石灰-酸化クロムの反応 : マグネシアの焼結に関する研究(第3報)
- 石灰-酸化鉄系化合物とマグネシアに対する挙動 : マグネシアの焼結に関する研究(第2報)
- マグネシアおよびマグネシオフェライトの酸溶解性 : マグネシアの焼結に関する研究(第1報)
- マグネシアの低温焼結に及ぼす添加剤の影響に関する研究
- マグネシア・クリンカーの熱衝撃抵抗
- マグネシア・クリンカーの耐消化性
- マグネシア・クリンカーの微構造に及ぼすCaO, SiO2およびFeO3添加の影響 (1-2)
- マグネシア・クリンカー内の生成物と微構造におよぼすCaO, SiO2, Fe2O3添加の影響 (その2) : MgO-SiO2-Fe2O3系, MgO-CaO-Fe2O3系, MgO-CaO-SiO2系
- 硬燒マグネシア中の添加酸化鐵の状態 (1)
- マグネシア・クリンカー内の生成物と微構造におよぼすCaO, SiO2添加の影響 (その1) : MgO-CaO, MgO-SiO2系
- 硬焼マグネシア中の添加酸化鉄の状態 (2)
- マグネシア・クリンカーに及ぼすMgO・Fe2O3, CaO・Fe2O3の鑛化作用について
- マグネシア・クリンカーにおける酸化鐵の鑛化作用について (その2)
- マグネシア・クリンカーにおける酸化鐵の鑛化作用について (その1)