マンガンよおびクロムの真空融解炉中におけるガス吸収について
スポンサーリンク
概要
- 論文の詳細を見る
There were discussions on the adsorption mechanisms of carbon monoxide by manganese in the vacuum fusion furnace. Thanheiser reported that manganese films deposited on the walls of the vacuum fusion furnace adsorbed carbon monoxide, while Wood <I>et al</I>. and Sawa reported that carbon monoxide adsorption by manganese occured when it was depositing. Carbon monoxide was allowed to circulate in a furnace and gas adsorption curves by manganese and chromium were measured at the different furnace conditions. By means of this method whether the adsorption of carbon monoxide occured at the depositing metal vapor or on the deposited films were partly clarified. Much more carbon monoxide was adsorbed by chromium vapor than chromium films on the furnace walls, although in the case of manganese it was adsorbed rather by films than vapor. The adsorption speed by manganese vapor was about 300 times greater than that by chromium vapor.<BR>In the analysis of steel samples containing manganese the adsorption mechanism by manganese might be affected by other components.<BR>These results will give useful informations for designing the apparatus.
- 社団法人 日本分析化学会の論文
著者
関連論文
- X線光電子スペクトル法による銅-ニッケル及びパラジウム-銀合金の表面組成分析における問題点
- レーザー誘起光音響検出法による水溶液中の過マンガン酸イオンの極微量定量
- 5-ヒドロキシキノリンのけい光寿命と励起状態の反応性
- 7-ヒドロキシクマリンのけい光の時間分解スペクトル
- セチルピリジニウムクロリド共存下で2-(2-チアゾリルアゾ)-5-ジメチルアミノフェノールによるトリウムの吸光光度定量
- スパークイオン源質量分析法による銀メンブラン・フィルター上に捕集した大気浮遊粉じん中の微量元素の分析
- 紫外スペクトルの吸収強度
- 放射線イオン化検出器による微量無機ガスの分析方法の研究
- 質量分析による有機化合物の構造解析法の研究 : 二,三の含酸素化合物について
- 冷原子―非分散原子けい光法による毛髪中の微量水銀の定量