Tribological properties of Ti-based (Ti, TiO<SUB>2</SUB> and TiN) films on the stainless steel (304SS) substrate were investigated in the atmosphere of N<SUB>2</SUB>, O<SUB>2</SUB> and air at several pressures. Films 0.2 μm thick were prepared on the mirror-polished substrate with an ion beam assisted deposition method, an ion beam assisted reactive deposition method and the dynamic ion mixing method. Tribological tests were carried out with a friction tester of Pin-On-Disk type in a high vacuum equipment. The wear surface was observed with an optical microscope, a scanning laser microscope and a scanning electron microscope.<BR>The friction coefficients of stainless steel, Ti, TiO<SUB>2</SUB> and TiN film increased with decreasing a pressure and those except of stainless steel converged on 0.3 in a pressure of 1 × 10<SUP>-3</SUP> Pa. In an O<SUB>2</SUB> atmosphere, the behavior of the Ti film in a friction coefficient for a pressure was similar to that of the TiO<SUB>2</SUB> film, and in a N<SUB>2</SUB> atmosphere, the friction coefficients of Ti and TiN film showed the same value. These results suggested the relation between a kind of a gas atmosphere in the tribological test and the film element.
論文 | ランダム
- 2D23 米国における競争的資金の会計制度とマネジメントの柔軟性 : 調査と考察(公的資金配分機関のマネジメント,一般講演,第22回年次学術大会)
- 24aWP-5 スピン・軌道秩序系における希釈効果と磁気構造(24aWP 多軌道系,フラストレーションなど,領域8(強相関係:高温超伝導,強相関f電子系など))
- 24pWF-2 t_軌道系における軌道状態の数値的研究(多軌道系(理論),領域8,強相関係:高温超伝導,強相関f電子系など)
- 19aPS-11 t_軌道系における軌道状態の数値的研究(19aPS 領域8ポスターセッション(低温),領域8(強相関系:高温超伝導,強相関f電子系など))
- 23aZG-4 量子軌道系における軌道秩序と希釈効果(23aZG 多軌道系・準一次元系など(理論),領域8(強相関系:高温超伝導,強相関f電子系など))