ヘリコンスパッタ法により作製したTiO<SUB>2</SUB>/SiO<SUB>2</SUB>多層膜の微細構造および光学特性
スポンサーリンク
概要
- 論文の詳細を見る
Alternating TiO<SUB>2</SUB>/SiO<SUB>2</SUB> multilayer optical films were fabricated on BK7 glass and Si (100) substrates by helicon plasma sputtering at room temperature. Optical and structural characterization of monolayers of TiO<SUB>2</SUB> and SiO<SUB>2</SUB> films, and their multilayers have been performed. The results of structural analysis show that the TiO<SUB>2</SUB> and SiO<SUB>2</SUB> films have a homogeneous and amorphous microstructure. Auger electron spectroscopy (AES) and transmission electron microscopy (TEM) observations reveal that TiO<SUB>2</SUB>/SiO<SUB>2</SUB> multilayer films have well-defined interface. Five layers of alternating TiO<SUB>2</SUB> and SiO<SUB>2</SUB> exhibit maximum reflectance of 87% around the central wavelength of 800 nm which agrees well with the theoretical result.
論文 | ランダム
- 8009 東大阪市における新築・戸建て住宅の敷地特性 : 大都市部における新築・戸建て住宅に関する研究 (その1)
- 住宅所有関係別家賃と地方性 : 住居・家賃に関する基礎的研究 その3
- 県別所得からみた住宅事情の分析 : 住居・家賃に関する基礎的研究 その2
- 20. 住宅所有関係別家賃と地方性 : 住居・家賃に関する基礎的研究 その2(計画系)
- 19. 県別所得からみた住宅事情の分析 : 住居・家賃に関する基礎的研究 その1(計画系)