メカニカルアロイングしたCu-Ti-B合金粉末の焼結
スポンサーリンク
概要
- 論文の詳細を見る
Sintering of Cu-8mass%Ti-4mass%B alloy powder prepared by mechanical alloying was carried out at temperature range of 673K to 1173K for various times. Changes of structure and mechanical strength of the sintered powder-compact with the sintering process were investigated by using of X-ray diffraction analysis, electron microscope, Vickers hardness test and 3-points-bending test. Hardness of the compact sintered at from 673K to 873K increases with the sintering time, but pore in the compact is not changed after the long sintering time. On the other hand, when the sintering was carried out at high temperature for short time, the hardness of the compact decreases and then reaches to constant value, but the density increases. Fracture strength of the sintered compact increases, and formation of the titanium diborid becomes more frequent with increasing of the sintering temperature. It is observed that the copper-rich phase forms at contact region between the particles in the compact sintered at high temperature, and it brings on the high fracture strength.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 216 放電プラズマ焼結法を利用した Mg_2Si 粒子分散型マグネシウム押出材の特性
- Mg_2Siの固相合成に及ぼす粉体特性および圧粉条件の影響
- 2914 メカニカルアロイングしたMg-Al合金粉末の型鍛造への応用(S34-2 粉末成形とその評価(2),S34 粉末成形とその評価)
- 2913 メカニカルアロイング粉末を用いて表面改質したマグネシウム合金の摩耗特性(S34-1 粉末成形とその評価(1),S34 粉末成形とその評価)
- 2912 切削チップを用いたメカニカルアロイング粉末による鋳鉄の表面改質(S34-1 粉末成形とその評価(1),S34 粉末成形とその評価)
- Al/Ni混合粉末の半溶融加工で作製した金属間化合物とその高温強度特性
- AI/Ni混合粉末の等速加熱にともなう金属間化合物の生成とその成形
- 6.2.材料加工(6.機械材料・材料加工)(機械工学年鑑)
- 機械材料・材料加工
- メカニカルアロイング粉末を用いたマグネシウム合金の表面改質 : 圧縮変形による接合