HIP法による圧電磁器の高密度化
スポンサーリンク
概要
- 論文の詳細を見る
It has been tried to densify PbTiO<SUB>3</SUB>-PbZrO<SUB>3</SUB>-Pb(Zn, Nb)O<SUB>3</SUB> piezoelectric ceramics by hot isostatic press(HIP)method.<BR>Specimens were set in the chamber of HIP equipment without any sealed containers and sintered at atcmperature of 900-1200°C under a pressure of 170-1600 kg/cm<SUP>2</SUP> in incrt gas atmospheres. Since the working gas was pure argon or nitrogen gas, the deoxidizing phenomenon was inevitable for some specimens in apart ofabatch. This phenomenon was easily observed by the change in color and the decrease ofelectrical resistivity. These deoxidized specimens were able to show the recovery by heat treatment at a temperatureof 800-1000°C in oxygen atmosphere. Isostatically hot pressed ceramics showed no defect on polished surface, the equivalent piezoelectric properties and a mechanical strength about 20% higher than that of thenormally sintered materials with a density of 97%.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- SrO-Sm_20_3-Ta_20_5系セラミックスの粒成長と誘電特性(セラミック材料)
- SrO-Sm2O3-Ta2O5系セラミックスの粒成長と誘電特性
- Microwave Characteristics of A(B1〓3+〓/2B1〓5+〓/2)O3 Ceramics〔A=Ba,Ca,Sr;B3+=La,Nd,Sm,Yb;B5+=Nb,Ta〕
- 圧電セラミックスの厚みすべり振動測定方法(技術資料)
- 複合ペロブスカイトCa(Ga_Ta_)O_3の生成とマイクロ波誘電特性 : 組成・構造
- HIP法による高透過率PLZTの合成と高速光スイッチへの応用研究
- PLZTのミクロ構造と電気光学効果
- 高密度・微粒子マンガン亜鉛フェライトとランタン置換チタン酸ジルコン酸鉛セラミックス(高圧力小特集)
- PLZTの圧電効果と透光性
- HIPにより作製したPLZT磁器の光スイッチング
- HIP法による圧電磁器の高密度化
- HIP法による圧電磁器の高密度化
- Hot Isostatic Pressing of PZT and PLZT Ceramics.