フェライト製造工程の粉末冶金的解析(第6報) : Ni・Znフェライトの焼結と磁気特性に及ぼす仮焼および粉砕条件の影響
スポンサーリンク
概要
- 論文の詳細を見る
The effects of powder processing conditions on the sintering of Ni.Zn ferrite have been . presented. The constituent oxide mixtures were calcined at temperatures between. 700 and. 1400°C, and then subjected to ball-milling up to 55 hours. Shrinkage, fired density and some magnetic properties were studied at different firing temperatures. It is shown that the. sintering behaviors, and hence the properties of sintered products could be interpreted adequately by powder parameters such as aggregation state of primary particle, size and its distribution. It is shown also that the effect of ball-milling is less significant unless the oxide mixtures are calcined above the recrystallization temperature.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- フェライトの熱力学
- 多相セラミックスの反応:(Zn_2TiO_4+TiO_2)-ZnO及び-CaCO_3系
- やさしく楽しい「セラミックス」を
- Zr-フトキシドの加水分解挙動に及ぼす溶媒の影響
- ゲータイトおよびその分解によって得られたヘマタイトの粉体特性(粉体小特集)
- Bi_2O_3-TiO_2 混合物からの Bi_4Ti_3O_ の生成
- 焼結に及ぼす粒子形状の影響 : ゲータイトから得られた Fe_2O_3 の焼結挙動
- Al_2TiO_5の共析変態の速度論的研究
- Cu-Fe-O 三元系の相平衡
- 溶融Cu-Mn合金と超硬合金との相互作用
- 溶融銅とWC-Co超硬合金との相互作用に及ぼすTaCおよびTiC添加の影響
- 溶融亜鉛とWC-Co超硬合金の相互作用
- PZTセラミックスの製造における混合方法の影響
- 粉体層の底圧による粉体の内部摩擦の測定
- ポリスチレン粉体の成形物の構造に及ぼす成形圧力および温度の影響
- BaCO3とGeO2の反応
- プラスチック粉体成形物の空孔構造
- 粉体の焼結特性に関する研究IV : ZnFe2O4の焼結に及ぼす原料α-Fe2O3粉体の影響
- 粉体の焼結特性に関する研究III : α-Fe2O3粉体のち密化挙動および昇温速度の影響
- 粉体の焼結特性に関する研究II : α-Fe2O3粉体の焼結
- 粉体の焼結特性に関する研究I : α-Fe2O3粉体のキャラクタリゼイション
- 球形炭酸カルシウム (バテライト) の生成と水中におけるカルサイトへの転移(粉体小特集)
- 溶融銅と超硬合金の相互作用におよぼす溶融銅への添加物効果
- 310 溶融銅と超硬合金の相互作用に及ぼす溶融銅への添加物効果
- (Cr-Al)二元系水酸化物からのコランダム相の生成
- 酢酸鉛とテトラエトキシシランから得られた複合アルコキシドの構造
- BaCO3-TiO2二元系固体反応の速度と機構に及ぼす反応物粒子の凝集の影響
- フェライト製造工程の粉末冶金的考察
- フェライト製造工程の粉末冶金的解析(第5報) : Mn-Znフェライトの結晶組織と磁気特性と関係
- フェライト製造工程の粉末冶金的解析(第6報) : Ni・Znフェライトの焼結と磁気特性に及ぼす仮焼および粉砕条件の影響
- フェライト系状態図について
- フェライト製造工程の粉末冶金的解析 : (第4報)フェライトの結晶成長(II)