Copper-ferrous ferrites were sintered under various conditions to elucidate the mechanism of discontinuous grain growth.<BR>Straight grain boundaries were observed in the discontinuously growing grains. This boundary was determined to be the (111) plane of growing grain. Dynamical consideration of the straight boundaries suggested the existence of a liquid phase. The existence of the liquid phase, which produces the straight boundaries and gives a large mobility to them, is considered to be the main cause of discontinuous grain growth.<BR>A possible new mechanism was proposed for the nucleation in the discontinuous grain growth. Final size of a giant grain produced by discontinuous grain growth was controlled by the initial grain size, firing temperature and oxygen content of samples.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- RP_2O_6(R;Mg, Ca, Ba)ガラス熔融体におけるクロムイオンの気相との酸化還元平衡
- Fe_2O_3-V_2O_5-P_2O_5 系ガラスの電気伝導
- Fe_2O_3あるいはCuOを含む鉛-硼酸ガラスの電気伝導および構造
- 銅フェライト焼結体の接合によるモデル粒界の形成とその性質
- CuO, TiO_2,Fe_2O_3を含むPbO-B_2O_3系熔融体の電気伝導度, 密度およびその構造
- PbO-B_2O_3,Na_2O-B_2O_3系熔融体の電気抵抗の周波数依存性と構造
- FeO-Fe_2O_3-RP_2O_6(R=Mg, Ca, Ba)系ガラス熔融体と気相との酸化還元平衡に及ぼす酸化鉄濃度の影響
- Fe_2O_3-RP_2O_6,TiO_2-RP_2O_6系(R=Mg, Ca, Ba)ガラス熔融体と気相との酸化還元平衡ならびにガラスの比抵抗
- PbO-SiO_2-Fe_2O_3系酸化物熔融体の電気伝導および構造
- 耐熱性結晶化ガラス質繊維の塩処理による結晶化の促進
- CaO・Al_2O_3・2 SiO_2-2 MgO・2 Al_2O_3・5 SiO_2-CaO・TiO_2・SiO_2系の結晶化強化ガラス : B_2O_3 添加の曲げ強度増進におよぼす影響
- 耐熱性結晶化 ガラス 質繊維の表面処理による結晶化の促進
- A9.CaO・TiO_2・SiO_2-CaO・Al_2O_3・2SiO_2-2MgO・2Al_2O_3・5SiO_2系結晶化強化ガラス(研究発表講演要旨)
- ガラス質面の耐熱度
- 岩綿の耐熱度の測定と耐熱岩綿の試作
- フェライトの発明と成長の80年
- 焼結フェライトの空隙形状に関する研究 (第1報)
- 焼結フェライトの空隙形状に関する研究(第2報)
- 高温におけるフェライト表面の挙動
- 銅フェライトの焼結における不連続粒成長
- Widmanstätten構造を利用した面方位決定