Superstructured alloy films composed of non-nitride layers and nitride layers such as Co-Nb-Z r/Co-Nb-Zr-N and Fe-Nb-B/Fe-Nb-B-N are prepared by N<SUB>2</SUB> reactive R F sputtering. S oft magnetic properties are obtained when the layer thickness is less than 15 nm for the films comprizing metal-metalloid elements and less than 30 nm for the films comprizing metal-metal elements. Layered structures of the obtained films remained even after annnealing up to 600 °C in the metal-metalloid alloy films, while they changed into weakly compositionally modulated structures in the metal-metal alloy films. These films show high permeabilities (>2000 at1 MHz) and high saturation magnetizations (4π Ms=13-15 kG) and are promizing magnetic core materials for VTR or computer heads.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- TMR素子の磁化反転磁界抑制の検討
- PtMnスピンバルブ膜の極薄酸化物層と下地層によるMR特性
- トンネル接合における磁気抵抗, 磁気特性のAlOx厚依存
- TMR素子の抗磁力の抑制
- FeSiAl/AlOx/FeCoトンネル接合の磁気抵抗
- FeSiAl酸化膜を用いた強磁性トンネル接合の検討
- 積層フェリ固定層を用いたα-Fe_2O_3系スピンバルブ膜の薄膜化と高ピンニング磁界化
- 29a-J-12 Co/Ru/Co積層フェリ固定層を用いたα-Fe_2O_3スピンバルブ膜のMR特性
- PRS法で作製したFeSi/FeSiO多層膜の軟磁気特性
- 酸化物反強磁性体α-Fe_2O_3を用いたデュアルスピンバルブのMR特性
- 鏡面反射によるGMR効果の増大
- パレス反応性スパッタリングによるFe/Fe-O人工格子膜作成と界面の熱安定性
- 2p-X-1 酸化物反射膜を用いたスピンバルブ膜のGMR特性
- MBE法により作製した〔Ni-Fe/Cu/Co〕膜のAgキャップ層によるMR比増加効果
- [NiCoFe/Cu/Co]スパッタ膜におけるCu/Ag反射膜によるGMR増大
- 界面反射膜によるMR比増大のシミュレーション
- CoMnBアモルファス合金を用いたスピンバルブ膜のMR特性
- スピンバルブ膜を用いたメモリー素子
- 金属人工格子膜の膜面垂直MR特性
- エピタキシャルM/Cu人工格子膜の磁気抵抗効果(M=NiFe,NiFeCo,CoFe)
- 超高真空蒸着装置で作製した金属人工格子薄膜の磁気特性
- スパッタアモルファスビデオヘッド
- Co-Metal系薄膜の軟磁気特性と熱安定性
- 研究の愉しさ
- 磁気ヘッド用人工格子合金