Mn-Znフェライトの生成反応に関する研究
スポンサーリンク
概要
- 論文の詳細を見る
An investigation has been made to elucidate the formation processes of manganese-zinc ferrites in the course of firing of raw materials by X-ray diffraction analysis and measurements of DTA as well as thermogravimetry. When Fe<SUB>2</SUB>O<SUB>3</SUB>, ZnO and MnO<SUB>2</SUB> were used as the starting, materials, the formation of ZnMn<SUB>2</SUB>O<SUB>4</SUB> proceeded preferentially at the early stage of firing in the range 580°-650°C.At temperatures, of 650° to 710°C, the reaction for the formation of ZnFe<SUB>2</SUB>O<SUB>4</SUB> was mainly conducted. The solid state reaction occurred among the formed ZnMn<SUB>2</SUB>O<SUB>4</SUB>, ZnFe<SUB>2</SUB>O<SUB>4</SUB> and remained Fe<SUB>2</SUB>O<SUB>3</SUB> at 800°-1200°C, and the stoichiometric Mn<SUB>1/2</SUB>Zn<SUB>1/2</SUB>Fe<SUB>2</SUB>O<SUB>4</SUB> was finally formed. It was also found that Mn<SUB>3</SUB>O<SUB>4</SUB> is less reactive than MnO<SUB>2</SUB>, MnCO<SUB>3</SUB> and Mn<SUB>2</SUB>O<SUB>3</SUB> for the formation of ZnMn<SUB>2</SUB>O<SUB>4</SUB> and that Mn<SUB>3</SUB>O<SUB>4</SUB> alone affords, an another formation process.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 超音波霧化法による灯油の触媒酸化 : 超音波ストーブの試作
- 還元鑞付け法によるフェライト磁わい振動子の接合とその音響振動法による評価
- フェライト振動子の鑞付け接合強度の音響振動法による評価
- 振動フィーダを用いた粉体供給装置の開発
- 振動による微粉体供給法に関する研究
- 超音波振動を用いた粉体の定量供給法
- 粉粒体供給に対する超音波振動の応用
- 溶媒抽出法を用いた高純度酸化鉄の製造
- Mn-Znフェライトの生成反応に関する研究
- 接合体の熱応力の解析(III)
- 接合体の熱応力の解析
- 接合体の熱応力の解析(II)