TiC0.7-N0.3-15Ni-8Mo合金の機械的および切削特性に及ぼす添加炭素量の影響
スポンサーリンク
概要
- 論文の詳細を見る
For the purpose of improving cutting properties of Ti(C, N) base cermet, the microstructure and several mechanical properties of TiC<SUB>0.7</SUB>N<SUB>0.3</SUB>-15Ni-8Mo alloy were investigated in relation to the change of additional carbon content. Moreover, in order to clarify the effect of additional carbon content and TiN addition on strengthening of the binder phase, the changes of Ti and Mo concentrations, hardness and lattice parameter of the binder phase of coarse grained TiC-(0, 5, 10, 20) TiN-30Ni-l5Mo alloys were investigated.<BR>The results obtained are as follows;<BR>(1) The growth of the intermediate phase formed around the core of the hard phase (TiC<SUB>0.7</SUB>N<SUB>0.3</SUB>) of TiC<SUB>0.7</SUB> N<SUB>0.3</SUB>-15M-8Mo alloy in sintering process was not appreciably affected by the change of additional carbon content.<BR>(2) The lattice parameter of the binder phase, hardness, transverse-rupture strength, compressive yield strength, and wear resistance in continuous cutting test in turning steel of TiC<SUB>0.7</SUB>N<SUB>0.3</SUB>-15Ni-8Mo alloy increased with decrease of additional cabon content.<BR>(3) Ti concentration in the binder phase of coarse grained TiC-30Ni-15Mo alloy was as much as 4-8% depending on the additional carbon content. On the other hand, Mo concentration was much lower, i.e. 0.5-1.0wt%. Furthermore, Mo concentration in the binder phase of the alloy increased remarkably by the partially replacement of TiC with TiN. In contrast, Ti concentration in the binder phase decreased by 25%-50% with the addition of TiN, the rate of the decrease being smaller with the alloy of lower carbon content.<BR>(4) The improvement of the mechanical and cutting properties of TiN bearing low carbon alloy was attributed to the effect of solid solution strengthening of the binder phase through greatly increased dissolution of Mo.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- TiC0.7N0.3-15Ni-8Mo合金の機械的および切削特性に及ぼすAlN添加の影響
- WC-(6-20)%Co合金の高温曲げ破壊特性に及ぼす歪み速度の影響
- WC-10%Co合金の高温曲げ破壊特性に及ぼす内在欠陥の影響
- HIPによって成形したRené95の組織と機械的特性
- Ti(C,N)-30Mo2C-13Ni-合金の諸特性に及ぼすN/(C+N)比の影響
- TiC0.7-N0.3-15Ni-8Mo合金の機械的および切削特性に及ぼす添加炭素量の影響
- TiC-15Ni-8Moサ-メットへのアルミニウム添加の微細構造,機械的性質に及ぼす影響