Influence of Macro/Microstructure on the Toughness of 'All Weld' Multipass Submerged Arc Welded C-Mn Steel Deposits.
スポンサーリンク
概要
- 論文の詳細を見る
'All weld' deposited rectangular blocks of C-Mn steel were prepared by the multipass submerged arc process, using different welding currents (500-750 A) and speeds (40-60 cm/min). A filler wire of 4 mm diameter and a basic agglomerated flux were employed. Varying the welding parameters influenced the macrostructure comprising coaxial dendrites and reheat refined regions whose amounts were determined by quantitative metallography. The influence of dendrite content, on the toughness as influenced by temperature and orientation of the specimens (LT, TS and SL) was assesed both in the as welded and in the heat treated (873 K) conditions.An increase in the area fraction of dendrites beyond about 37% adversely affected the toughness which was found to be lowest in the LT direction. A post weld heat treatment carried out at 873 K improved the overall toughness due to spheroidization of cementite, especially within the refined equiaxed regions, resulting from 'reheating' during multipass deposition.
- The Iron and Steel Institute of Japanの論文
著者
-
Patwardhan A.
Department Of Endodontics University Of Texas Health Science Center At San Antonio
-
Ghosh P.
Welding Research Laboratory Department Of Mechanical And Industrial Engineering University Of Roorke
-
GHOSH P.
Welding Research Laboratory, Department of Mechanical and Industrial Engineering, University of Roorkee
-
Yongyuth P.
Welding Research Laboratory, Department of Mechanical and Industrial Engineering, University of Roorkee
-
Gupta P.
Welding Research Laboratory, Department of Mechanical and Industrial Engineering, University of Roorkee
-
Prakash Satya
Department of Metallurgical Engineering, University of Roorkee
-
Yongyuth P.
Welding Research Laboratory, Department of Mechanical & Industrial Engineering, University of Roorkee
-
Gupta P.
Welding Research Laboratory, Department of Mechanical & Industrial Engineering, University of Roorkee
関連論文
- Trigeminal Nociceptors Express Prostaglandin Receptors
- Geometrical Characteristics of Pulsed Current Positional GMA Weld
- Fracture Properties of Multipass Submerged Arc Weld of HSLA Steel Produced by Using Flux Cored Filler Wire
- Characteristics of Pulsed Current Bead on Plate Deposit in Flux Cored GMAW Process
- Influence of Macro/Microstructure on the Toughness of 'All Weld' Multipass Submerged Arc Welded C-Mn Steel Deposits.
- Two Dimensional Spatial Geometric Solution for Estimating the Macroconstituents Affecting the Mechanical Properties of Mulitpass C-Mn Steel SAW Deposits.
- Thermal cycle and microstructure of heat affected zone(HAZ) of flash butt welded Mn-Cr-Mo dual phase steel.
- Influence of Heat Treatment on the Properties of Wear Resistant Tungsten Carbide Embedded Nickel Base Coating Produced by Gas Thermal Spray Process.
- Influence of Weld Thermal Cycle on Properties of Flash Butt Welded Mn-Cr-Mo Dual Phase Steel.