Rates of Nitrogen and Carbon Removal from Liquid Iron in Low Content Region under Reduced Pressures.
スポンサーリンク
概要
- 論文の詳細を見る
The kinetics of nitrogen and carbon removal from a liquid iron surface in low content regions by blowing Ar gas mixture under reduced pressures have been studied using the same vacuum induction furnace at 1 600°C, respectively. The results obtained are as follows:(1) The nitrogen removal reaction is described as a second order reaction with respect to nitrogen content. The overall reaction rate constant, kovN, decreases with the increase of total pressure, and oxygen and sulfur content.Assuming that the nitrogen removal reaction progresses by a mixed control and that the chemical reaction for nitrogen gas formation is caused by adsorbed nitrogen atoms, the chemical reaction rate constant, krN, and the adsorption coefficient of oxygen, κO, and of sulfur, κS, are estimated as follows:N+N=N2+_??_krN(=k[N]/fN2) cm/mass%/sec = 15/(1+κO·aO+κS·aS)2, κO=161, κS=63.4In the Fe-20mass%Cr-0.2Mass%C-S system also, the value of krN can be expressed by the same equation. It is thus concluded that, macroscopically, the mechanism of nitrogen removal is the same irrespective of whether or not the melt contains chromium.(2) In the carbon content range below 200 ppm, the overall carbon removal reaction rate constant, kovC, exhibits a maximum value against oxygen content, and decreases with the increase of sulfur content.Assuming that the chemical reaction for CO gas formation caused by the adsorbed carbon and the adsorbed oxygen atoms as a following equation, the dependence of the chemical reaction rate constant on oxygen and sulfur content is explained by the values of the adsorption coefficients κO and κS, respectively.C+O=CO+_??_The value of κO is equal to about 100-300 and that of κS is equal to about 40-65.These values are in general accord with those determined from the nitrogen desorption reaction.
- The Iron and Steel Institute of Japanの論文
The Iron and Steel Institute of Japan | 論文
- The Evolution of Precipitates in Nb-Ti Microalloyed Steels during Solidification and Post-solidification Cooling
- Short Contribution to the Study of the Washing Effect in Electromagnetic Stirrers for Continuous Casting
- Nitrogen Bearing Martensitic Stainless Steels : Microstructure and Properties
- A Two-dimensional Finite Element Thermomechanical Approach to a Global Stress-Strain Analysis of Steel Continuous Casting
- Transformation Behavior and Microstructures in Ultra-low Carbon Steels