Transformation behavior of nickel-titanium orthodontic wires under tensile load
スポンサーリンク
概要
- 論文の詳細を見る
This study investigated transformations of nickel-titanium wires using differential scanning calorimetry (DSC) and thermomechanical analysis (TMA) under tensile load (100 gf or 500 gf). Two nickel-titanium wires, 35°C Copper Ni-Ti and Nitinol SE, were selected. DSC analyses were performed between –90° and 100°C. Specimens prepared for TMA were approximately 150 μm thick and 12 mm long. TMA analyses were performed between –120° and 100°C. With TMA, all transformation temperatures for a tensile load of 500 gf, obtained from both the heating and cooling curves, were higher than those for a tensile load of 100 gf. While mean As and Af temperatures for Copper Ni-Ti obtained by TMA were much higher than those obtained by DSC analysis, mean Ms and Mf temperatures obtained by TMA were much lower than those obtained by DSC analysis. The transformation behavior of nickel-titanium wires with change in temperature was affected by application of tensile load.
論文 | ランダム
- 各種高血圧疾患における末梢血コルチゾン/コルチゾール濃度比の変動
- カルバマゼピン投与後に抗利尿ホルモン不適合分泌症候群(SIADH)を呈した糖尿病の一例
- 外来診療における1, 5アンヒドログルシトールの意義
- 23C-11 グリチルリチン製剤が原因と疑われた低 K 血症の 1 例
- 正常および実験的糖尿病ラットの組織内ソルビトール含量 : 高速液体クロマトグラフィーを用いた新しい測定法