方向性電磁鋼板の磁気特性におよぼすTiN高張力被膜の影響
スポンサーリンク
概要
- 論文の詳細を見る
The influence of crystal orientation on the magnetic properties of 3% Si-Fe single crystals was investigated by measuring iron losses and observing magnetic domain patterns in TiN-coated and chemically polished specimens. The iron loss was reduced in a TiN-coated sample whose β angle was less than 4 degrees and increased in a sample whose β angle was larger than 4 degrees. The improvement in the iron loss was due to a decrease in eddy current loss that corresponded to a decrease in the magnetic domain width caused by the tensile stress effect of the TiN coating. In the sample whose β angle was larger than 4 degrees, the eddy current loss did not change due to the TiN coating because the magnetic domain width was almost the same under alternate magnetization. Additionally, hysteresis loss increased because of increase magnetic coercive force.
著者
-
岡部 誠司
JFEスチール(株)スチール研究所
-
新垣 之啓
JFEスチール(株)スチール研究所
-
岡部 誠司
川崎製鉄(株)技術研究所
-
岡部 誠司
Jfeスチール
-
岡部 誠司
JFEスチール株式会社スチール研究所
-
新垣 之啓
JFEスチール株式会社スチール研究所
関連論文
- 3%Si-Fe単結晶の磁気特性におよぼす引張応力と表面性状の影響-2
- 3%Si-Fe単結晶の磁気特性におよぼす引張応力と表面性状の影響
- 3%Si-Fe単結晶の磁気特性におよぼす引張応力と表面性状の影響
- 三相積鉄心モデルトランスによる騒音の解析 (電磁鋼板特集号)
- 3相積変圧器モデル鉄心特性に及ぼす局所磁束波形の影響
- 3相積変圧器モデル鉄心における局所磁気特性および騒音の解析 (電磁鋼板小特集号)
- 三相積鉄心変圧器のT接合部モデルの局所磁束測定
- 三相積変圧器のT接合部モデルにおける局所磁束
- 三相積鉄心のT接合部モデルの局所磁束測定
- 方向性電磁鋼板の磁気特性におよぼすTiN高張力被膜の影響
- 直流偏磁したモデル変圧器の鉄損、騒音特性
- 直流偏磁したモデル変圧器の鉄損、騒音特性 (第2報)