Equilibrium between Ti and O in Molten Fe–Ni, Fe–Cr and Fe–Cr–Ni Alloys Equilibrated with ‘Ti3O5’ Solid Solution
スポンサーリンク
概要
- 論文の詳細を見る
The Ti deoxidation equilibrium of Fe–Ni, Fe–Cr and Fe–Cr–Ni alloys saturated with ‘Ti3O5’ and Ti2O3 phase was clarified in previous researches. Solubility of Fe, Cr and/or Ni oxides in ‘Ti3O5’ phase equilibrated with liquid Fe–Ni, Fe–Cr and Fe–Cr–Ni alloys at 1823 K to 1923 K were measured by SEM–EDS. It was confirmed that the solubility of Fe, Cr and/or Ni oxide in ‘Ti3O5’ phase at low Ti content increase with decrease of Ti content in alloys. Titanium content that dissolution of Fe, Cr and/or Ni oxide into ‘Ti3O5’ phase becomes apparent increases with increase of Cr and/or Ni content of the alloys. The activity of Ti deoxidation product, ‘Ti3O5’ phase, equilibrated with Fe–Ni, Fe–Cr and Fe–Cr–Ni alloys was also evaluated by Redlich-Kister type polynomial. Equilibrium between Ti and O at low Ti content of those alloys was analyzed using the activity of ‘Ti3O5’ phase.
論文 | ランダム
- C121 電子機器用水冷システムの放熱特性評価
- いわゆる胆管内発育型肝細胞癌
- 造血因子 (成長因子)
- 「日新は会合に出ないが情報は伝わっていた」審査官尋問に長谷川参考人 (「日新製鋼」に対する第7回審判で参考人審尋 公取委--鋼板カルテル事件 JFE鋼板から1名、淀川製鋼所から2名出廷)
- 日新製鋼に合意内容伝えたのは「Aさんと思っている」と石田参考人 (「日新製鋼」に対する第7回審判で参考人審尋 公取委--鋼板カルテル事件 JFE鋼板から1名、淀川製鋼所から2名出廷)